Umum
| Properti | Suhu | Nilai |
|---|---|---|
| Kepadatan | 23,0 °C | 8,5 g/cm |
Mekanik
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Modulus elastisitas | 23,0 °C | 102 IPK | |
| Perpanjangan | 23,0 °C | 20% | |
| Kekerasan, Brinell | 23,0 °C | 90 [-] | |
| Kekerasan, Vickers | 23,0 °C | 90 [-] | |
| Modulus geser | 23,0 °C | 40 IPK | Khas untuk Tembaga Tempa Kuningan |
| Kekuatan tarik | 23,0 °C | 360 MPa | |
| Kekuatan hasil Rp0.2 | 23,0 °C | 180 MPa |
Termal
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Koefisien ekspansi termal | 20,0 °C | 2.06E-5 1/K | |
| 100.0 °C | 2.06E-5 1/K | ||
| Titik leleh | 885 - 900 °C | ||
| Kapasitas panas spesifik | 23,0 °C | 371 - 418 J/(kg·K) | Khas untuk Tembaga Tempa Kuningan |
| Konduktivitas termal | 23,0 °C | 100 W/(m·K) | |
Listrik
| Properti | Suhu | Nilai |
|---|---|---|
| Konduktivitas listrik | 23,0 °C | 1,47E+7 S/m |
| Resistivitas listrik | 23,0 °C | 6.8E-8 ·m |
Sifat kimia
| Properti | Nilai |
|---|---|
| Aluminium | 0,05% |
| Tembaga | 60 - 62% |
| Besi | 0,3% |
| Memimpin | 2,5 - 3,5% |
| Nikel | 0,3% |
| Lainnya | Istirahat Zn, total 0,2 |
| Timah | 0,2% |
Logam
Properti Umum Properti Suhu Nilai Kepadatan 23,0 °C 7,6 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23,0 °C 119 IPK Perpanjangan 23,0 °C 7 - 13% Kekerasan, Brinell 23,0 °C 140 - 150 [-] Rasio Poisson 23,0 °C 0.34 [-]
Properti Umum Properti Suhu Nilai Kepadatan 23,0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Modulus elastisitas 23,0 °C 130 IPK Perpanjangan 23,0 °C 25% Kekerasan, Vickers 23,0 °C 90 [-] Kekuatan tarik 23,0 °C 300 MPa Kekuatan hasil Rp0.2
Properti Umum Properti Suhu Nilai Kepadatan 23.0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23.0 °C 95 - 98 IPK Khas untuk Tembaga Tempa Murni / Tembaga Paduan Rendah Perpanjangan 23.0 °C 33% Kekerasan, Vickers 23.0 °C 55
Properti Umum Properti Suhu Nilai Kepadatan 23.0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23.0 °C 120 IPK Perpanjangan 23.0 °C 7% Perpanjangan A100 23.0 °C 3% Kekerasan, Brinell 23.0 °C 90 [-] Kekerasan, V