Umum
| Properti | Suhu | Nilai |
|---|---|---|
| Kepadatan | 23,0 °C | 8,1 g/cm³ |
Mekanik
| Properti | Suhu | Nilai |
|---|---|---|
| Modulus elastisitas | 23,0 °C | 93 IPK |
| Perpanjangan | 23,0 °C | 15% |
| Kekerasan, Brinell | 23,0 °C | 150 [-] |
| Kekerasan, Vickers | 23,0 °C | 150 [-] |
| Kekuatan tarik | 23,0 °C | 540 MPa |
| Kekuatan hasil Rp0.2 | 23,0 °C | 280 MPa |
Termal
| Properti | Suhu | Nilai |
|---|---|---|
| Koefisien ekspansi termal | 20,0 °C | 2.04E-5 1/K |
| 100.0 °C | 2.04E-5 1/K | |
| Titik leleh | 865 - 885 °C | |
| Konduktivitas termal | 23,0 °C | 63 W/(m·K) |
Listrik
| Properti | Suhu | Nilai |
|---|---|---|
| Konduktivitas listrik | 23,0 °C | 7.80E+6 S/m |
| Resistivitas listrik | 23,0 °C | 1.28E-7 ·m |
Sifat kimia
| Properti | Nilai |
|---|---|
| Aluminium | 1,3 - 2,3% |
| Tembaga | 57 - 59% |
| Besi | 1% |
| Memimpin | 0,2 - 0,8% |
| Mangan | 1,5 - 3% |
| Nikel | 1% |
| Lainnya | Istirahat Zn, total 0,3 |
| Silikon | 0,3 - 1,3 % |
| Timah | 0,4% |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | mematri keras :wenig geeignnet, mematri lunak:wenig geeignet | |
| Kemampuan Kerja | Derajat pembentukan dingin antara anil:maks. 15%, umum (kondisi):terbatas | |
Logam
Properti Umum Properti Suhu Nilai Kepadatan 23,0 °C 7,6 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23,0 °C 119 IPK Perpanjangan 23,0 °C 7 - 13% Kekerasan, Brinell 23,0 °C 140 - 150 [-] Rasio Poisson 23,0 °C 0.34 [-]
Properti Umum Properti Suhu Nilai Kepadatan 23,0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Modulus elastisitas 23,0 °C 130 IPK Perpanjangan 23,0 °C 25% Kekerasan, Vickers 23,0 °C 90 [-] Kekuatan tarik 23,0 °C 300 MPa Kekuatan hasil Rp0.2
Properti Umum Properti Suhu Nilai Kepadatan 23.0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23.0 °C 95 - 98 IPK Khas untuk Tembaga Tempa Murni / Tembaga Paduan Rendah Perpanjangan 23.0 °C 33% Kekerasan, Vickers 23.0 °C 55
Properti Umum Properti Suhu Nilai Kepadatan 23.0 °C 8,9 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas 23.0 °C 120 IPK Perpanjangan 23.0 °C 7% Perpanjangan A100 23.0 °C 3% Kekerasan, Brinell 23.0 °C 90 [-] Kekerasan, V