DIN 17460 Grade X3CrNiMoN17-13 solusi anil (+AT)

-100.0 °C

206 IPK

20,0 °C

196 - 198 IPK

100.0 °C

190 - 192 IPK

200,0 °C

182 - 183 IPK

300,0 °C

174 - 175 IPK

400,0 °C

166 - 167 IPK

500,0 °C

158 - 159 IPK

600,0 °C

150 IPK

700.0 °C

142 IPK

800,0 °C

134 IPK

900,0 °C

127 IPK

1000.0 °C

120 IPK

20,0 °C

260 MPa

100.0 °C

205 MPa

200,0 °C

170 MPa

300,0 °C

148 MPa

400,0 °C

134 MPa

500,0 °C

127 MPa

550,0 °C

124 MPa

600,0 °C

121 MPa

20,0 °C

300 MPa

100.0 °C

240 MPa

200,0 °C

200 MPa

300,0 °C

178 MPa

400,0 °C

164 MPa

500,0 °C

157 MPa

550,0 °C

154 MPa

600,0 °C

151 MPa

-100.0 °C

1.49E-5 1/K

20,0 °C

1.61E-5 1/K

100.0 °C

1.61E-5 - 1.67E-5 1/K

200,0 °C

1.69E-5 - 1.72E-5 1/K

300,0 °C

1.73E-5 - 1.77E-5 1/K

400,0 °C

1.78E-5 - 1.81E-5 1/K

500,0 °C

1.82E-5 - 1.84E-5 1/K

600,0 °C

1.85E-5 - 1.88E-5 1/K

700.0 °C

1.87E-5 - 1.91E-5 1/K

800,0 °C

1.94E-5 1/K

900,0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

-100.0 °C

440 J/(kg·K)

20,0 °C

450 - 472 J/(kg·K)

100.0 °C

487 J/(kg·K)

200,0 °C

503 J/(kg·K)

300,0 °C

512 J/(kg·K)

400,0 °C

520 J/(kg·K)

500,0 °C

530 J/(kg·K)

600,0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800,0 °C

559 J/(kg·K)

900,0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

20,0 °C

13,5 - 16 W/(m·K)

100.0 °C

15 W/(m·K)

200,0 °C

16,7 W/(m·K)

300,0 °C

18,3 W/(m·K)

400,0 °C

19,8 W/(m·K)

500,0 °C

21,2 W/(m·K)

600,0 °C

22,7 W/(m·K)

700.0 °C

24.1 W/(m·K)

800,0 °C

25,5 W/(m·K)

900,0 °C

26,9 W/(m·K)

1000.0 °C

28,3 W/(m·K)

20,0 °C

3,6 mm²/dtk

100.0 °C

3,8 mm²/s

200,0 °C

4 mm²/s

300,0 °C

4,4 mm²/dtk

400,0 °C

4,6 mm²/s

500,0 °C

4,7 mm²/s

600,0 °C

4,9 mm²/dtk

700.0 °C

5,2 mm²/s

800,0 °C

5,5 mm²/dtk

900,0 °C

5,8 mm²/s

1000.0 °C

5,9 mm²/s