Baja tahan karat X5CrNiMo17-12-2 biasanya digunakan sebagai kawat yang ditarik dingin dengan diameter hingga 10 mm untuk pegas atau bagian pegas. Ini tahan korosi tertinggi dan berlaku hingga 250 °C.
Umum
| Properti | Suhu | Nilai |
|---|---|---|
| Kepadatan | 20,0 °C | 7,96 g/cm³ |
| 22.0 °C | 7,96 g/cm³ | |
Mekanik
| Properti | Suhu | Nilai |
|---|---|---|
| Modulus elastisitas | -100.0 °C | 206 IPK |
| 20,0 °C | 175 - 196 IPK | |
| 22.0 °C | 196.2 IPK | |
| 24.0 °C | 193.1 - IPK 197.9 | |
| 100.0 °C | 190 IPK | |
| 149,0 °C | 184,8 - 190,3 IPK | |
| 200,0 °C | IPK 182 | |
| 260.0 °C | 182 - 182,7 IPK | |
| 300,0 °C | 174 IPK | |
| 371,0 °C | 174,4 - 179,3 IPK | |
| 400,0 °C | 166 IPK | |
| 483.0 °C | 163,4 - 165,5 IPK | |
| 500,0 °C | 158 IPK | |
| 593.0 °C | 153,4 - 157,9 IPK | |
| 600,0 °C | 150 IPK | |
| 700.0 °C | 142 IPK | |
| 704.0 °C | 143,4 - 146.2 IPK | |
| 800,0 °C | 134 IPK | |
| 816.0 °C | 124.1 - 133.1 IPK | |
| 900,0 °C | 127 IPK | |
| 1000.0 °C | 120 IPK | |
| Rasio Poisson | 20,0 °C | 0.3 [-] |
| 22.0 °C | 0,29 [-] | |
| 24.0 °C | 0,23 - 0,28 [-] | |
| 149,0 °C | 0,24 - 0,28 [-] | |
| 260.0 °C | 0,28 - 0,31 [-] | |
| 371,0 °C | 0,33 - 0,36 [-] | |
| 483.0 °C | 0,29 - 0,32 [-] | |
| 593.0 °C | 0.32 [-] | |
| 704.0 °C | 0,28 - 0,34 [-] | |
| 816.0 °C | 0,22 - 0,27 [-] | |
| Modulus geser | 20,0 °C | 68 - 71 IPK |
| 22.0 °C | 75.8 IPK | |
| 24.0 °C | 77.2 - 78.6 IPK | |
| 149,0 °C | 74.5 IPK | |
| 260.0 °C | 69,6 - 71 IPK | |
| 371,0 °C | 64,1 - 67.6 IPK | |
| 483.0 °C | 62.1 - 64,1 IPK | |
| 593.0 °C | 57,9 - 60 IPK | |
| 704.0 °C | 54,5 - 55,9 IPK | |
| 816.0 °C | 51 - IPK 52,4 | |
| Kekuatan tarik | 20,0 °C | 1050 - 1990 MPa |
Termal
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Koefisien ekspansi termal | -100.0 °C | 1.49E-5 1/K | |
| 20,0 °C | 1.61E-5 1/K | ||
| 100.0 °C | 1.67E-5 1/K | ||
| 200,0 °C | 1.72E-5 1/K | ||
| 300,0 °C | 1.77E-5 1/K | ||
| 400,0 °C | 1.81E-5 1/K | ||
| 500,0 °C | 1.84E-5 1/K | ||
| 600,0 °C | 1.88E-5 1/K | ||
| 700.0 °C | 1.91E-5 1/K | ||
| 800,0 °C | 1.94E-5 1/K | ||
| 900,0 °C | 1.97E-5 1/K | ||
| 1000.0 °C | 2E-5 1/K | ||
| Suhu layanan maksimum, lama | -100 - 270 °C | ||
| Titik leleh | 1230 - 1480 °C | Khas untuk Baja Tahan Karat Austenitik | |
| Kapasitas panas spesifik | -100.0 °C | 440 J/(kg·K) | |
| 20,0 °C | 472 J/(kg·K) | ||
| 100.0 °C | 487 J/(kg·K) | ||
| 200,0 °C | 503 J/(kg·K) | ||
| 300,0 °C | 512 J/(kg·K) | ||
| 400,0 °C | 520 J/(kg·K) | ||
| 500,0 °C | 530 J/(kg·K) | ||
| 600,0 °C | 541 J/(kg·K) | ||
| 700.0 °C | 551 J/(kg·K) | ||
| 800,0 °C | 559 J/(kg·K) | ||
| 900,0 °C | 565 J/(kg·K) | ||
| 1000.0 °C | 571 J/(kg·K) | ||
| Konduktivitas termal | 20,0 °C | 13.3 W/(m·K) | |
| 100.0 °C | 14,9 W/(m·K) | ||
| 200,0 °C | 16,5 W/(m·K) | ||
| 300,0 °C | 18.1 W/(m·K) | ||
| 400,0 °C | 19,5 W/(m·K) | ||
| 500,0 °C | 21 W/(m·K) | ||
| 600,0 °C | 22.4 W/(m·K) | ||
| 700.0 °C | 23,8 W/(m·K) | ||
| 800,0 °C | 25,2 W/(m·K) | ||
| Difusivitas termal | 20,0 °C | 3,5 mm²/dtk | |
| 100.0 °C | 3,8 mm²/s | ||
| 200,0 °C | 4 mm²/s | ||
| 300,0 °C | 4,3 mm²/s | ||
| 400,0 °C | 4,5 mm²/dtk | ||
| 500,0 °C | 4,7 mm²/s | ||
| 600,0 °C | 4,8 mm²/s | ||
| 700.0 °C | 5,1 mm²/s | ||
| 800,0 °C | 5,4 mm²/s | ||
Listrik
| Properti | Suhu | Nilai |
|---|---|---|
| Resistivitas listrik | 20,0 °C | 7.91E-7 ·m |
| 100.0 °C | 8.45E-7 ·m | |
| 200,0 °C | 9.19E-7 ·m | |
| 300,0 °C | 9.77E-7 ·m | |
| 400,0 °C | 1.03E-6 ·m | |
| 500,0 °C | 1.08E-6 ·m | |
| 600,0 °C | 1.12E-6 ·m | |
| 700.0 °C | 1.15E-6 ·m | |
| 800,0 °C | 1.18E-6 ·m | |
Sifat kimia
| Properti | Nilai |
|---|---|
| Karbon | 0,07 % |
| Kromium | 16,5 - 18,5% |
| Mangan | 2% |
| Molibdenum | 2 - 2,5 % |
| Nikel | 10 - 13% |
| Nitrogen | 0,11 % |
| Fosfor | 0,05% |
| Silikon | 1% |
| Belerang | 0,015% |
Properti teknologi
| Properti | ||
|---|---|---|
| Fitur | Musim semi | |
Logam
Baja 28 Cr 4 cocok untuk bagian yang lebih kecil dengan beban yang sedikit lebih tinggi dalam pembuatan kendaraan, mesin dan teknik mesin (misalnya roda gigi transmisi, poros penggerak). Suhu aplikasi terendah. -25 °C. Properti Umum Properti Suhu Nilai Kepadatan 20,0 °C 7,83 g/cm³
Baja X 5 CrNiMo 17 12 2 sangat cocok untuk pembentukan dingin, kita harus menyadari peningkatan pengerasan regangan dingin dibandingkan dengan baja karbon. Peningkatan ketahanannya terhadap asam dan zat non-pengoksidasi yang mengandung halogen dan kemampuannya untuk dipoles dengan kilap tinggi memun
Baja tahan karat X7CrNiAl17-7 biasanya digunakan sebagai kawat yang ditarik dingin dengan diameter hingga 10 mm untuk pegas atau bagian pegas. Ini memiliki kekuatan kelelahan yang tinggi dan kekuatan suhu tinggi yang meningkat, tetapi ketahanan korosi yang berkurang dan dapat diterapkan hingga 300 °
Baja tahan karat X10CrNi18-8 biasanya digunakan ditarik dingin sebagai kawat berdiameter hingga 10 mm untuk pegas atau bagian pegas. Tahan terhadap korosi dan dapat diterapkan hingga 250 °C. Properti Umum Properti Suhu Nilai Kepadatan 20,0 °C 7,92 g/cm³ Mekanik Properti Suhu Nilai