Aplikasi untuk bagian dengan beban mekanis tinggi, seperti bel anil, sangkar anil, kotak sementasi dan pengerasan. Tahan panas:hingga 850 °C (suhu aplikasi tertinggi di udara)
Umum
| Properti | Suhu | Nilai |
|---|---|---|
| Kepadatan | 20,0 °C | 7,9 - 7,92 g/cm³ |
Mekanik
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Modulus elastisitas | -100.0 °C | 206 IPK | |
| 20,0 °C | 196 IPK | ||
| 100.0 °C | 190 IPK | ||
| 200,0 °C | IPK 182 | ||
| 300,0 °C | 174 IPK | ||
| 400,0 °C | 166 IPK | ||
| 500,0 °C | 158 IPK | ||
| 600,0 °C | 150 IPK | ||
| 700.0 °C | 142 IPK | ||
| 800,0 °C | 134 IPK | ||
| Perpanjangan | 20,0 °C | 40% | |
| Perpanjangan A80 | 20,0 °C | 40% | |
| Kekerasan, Brinell | 20,0 °C | 215 [-] | |
| Rasio Poisson | 23.0 °C | 0.3 [-] | Khas untuk Baja Tahan Karat Austenitik |
| Modulus geser | 23.0 °C | 77 IPK | Khas untuk Baja Tahan Karat Austenitik |
| Kekuatan tarik | 20,0 °C | 500 - 720 MPa | |
| Kekuatan hasil Rp0.2 | 20,0 °C | 190 MPa | |
| Kekuatan hasil Rp1.0 | 20,0 °C | 230 MPa | |
Termal
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Koefisien ekspansi termal | -100.0 °C | 1.49E-5 1/K | |
| 20,0 °C | 1.61E-5 1/K | ||
| 100.0 °C | 1.67E-5 1/K | ||
| 200,0 °C | 1.7E-5 - 1.72E-5 1/K | ||
| 300,0 °C | 1.77E-5 1/K | ||
| 400,0 °C | 1.8E-5 - 1.81E-5 1/K | ||
| 500,0 °C | 1.84E-5 1/K | ||
| 600,0 °C | 1.85E-5 - 1.88E-5 1/K | ||
| 700.0 °C | 1.91E-5 1/K | ||
| 800,0 °C | 1.9E-5 - 1.94E-5 1/K | ||
| Suhu layanan maksimum, lama | 0 - 850 °C | ||
| Titik leleh | 1230 - 1480 °C | Khas untuk Baja Tahan Karat Austenitik | |
| Kapasitas panas spesifik | -100.0 °C | 440 J/(kg·K) | |
| 20,0 °C | 472 - 500 J/(kg·K) | ||
| 100.0 °C | 487 J/(kg·K) | ||
| 200,0 °C | 503 J/(kg·K) | ||
| 300,0 °C | 512 J/(kg·K) | ||
| 400,0 °C | 520 J/(kg·K) | ||
| 500,0 °C | 530 J/(kg·K) | ||
| 600,0 °C | 541 J/(kg·K) | ||
| 700.0 °C | 551 J/(kg·K) | ||
| 800,0 °C | 559 J/(kg·K) | ||
| Konduktivitas termal | 20,0 °C | 13,9 - 15 W/(m·K) | |
| 100.0 °C | 15.4 W/(m·K) | ||
| 200,0 °C | 17,2 W/(m·K) | ||
| 300,0 °C | 18,7 W/(m·K) | ||
| 400,0 °C | 20.2 W/(m·K) | ||
| 500,0 °C | 21,6 W/(m·K) | ||
| 600,0 °C | 23 W/(m·K) | ||
| 700.0 °C | 24.4 W/(m·K) | ||
| 800,0 °C | 25.8 W/(m·K) | ||
| Difusivitas termal | 20,0 °C | 3,7 mm²/s | |
| 100.0 °C | 3,9 mm²/dtk | ||
| 200,0 °C | 4,2 mm²/s | ||
| 300,0 °C | 4,5 mm²/dtk | ||
| 400,0 °C | 4,7 mm²/s | ||
| 500,0 °C | 4,8 mm²/s | ||
| 600,0 °C | 5 mm²/s | ||
| 700.0 °C | 5,3 mm²/s | ||
| 800,0 °C | 5,6 mm²/dtk | ||
Listrik
| Properti | Suhu | Nilai |
|---|---|---|
| Resistivitas listrik | 20,0 °C | 7.3E-7 - 7.35E-7 ·m |
| 100.0 °C | 8E-7 ·m | |
| 200,0 °C | 8.68E-7 ·m | |
| 300,0 °C | 9.33E-7 ·m | |
| 400,0 °C | 9.89E-7 ·m | |
| 500,0 °C | 1.04E-6 ·m | |
| 600,0 °C | 1.08E-6 ·m | |
| 700.0 °C | 1.12E-6 ·m | |
| 800,0 °C | 1.15E-6 ·m | |
Sifat kimia
| Properti | Nilai |
|---|---|
| Karbon | 0,1% |
| Kromium | 17 - 19 % |
| Mangan | 2% |
| Nikel | 9 - 12% |
| Fosfor | 0,05% |
| Silikon | 1% |
| Belerang | 0,015% |
| Titanium | 0,8% |
Logam
Baja tahan panas X12CrNi23-13, mat. No 1.4833, tahan di udara hingga 1000 °C (suhu aplikasi tertinggi). Resistensi rendah terhadap gas belerang (mengurangi serta mengoksidasi). Berarti ketahanan terhadap nitrogen, gas kekurangan oksigen dan karburisasi. Bahan ini ideal untuk pengelasan menurut semua
Aplikasi untuk bagian dalam tungku industri, ketel uap, pabrik minyak bumi, untuk tabung selubung termometer. Resistensi terbaik terhadap nitrogen, gas kekurangan oksigen. Tahan panas di udara hingga 1050 °C.(suhu aplikasi tertinggi). Properti Umum Properti Suhu Nilai Kepadatan 20,0 °C 7
X15CrNiSi25-20 menunjukkan ketahanan penskalaan hingga maks. 1150 °C (suhu aplikasi tertinggi di udara). Baja ini sedikit tahan terhadap atmosfir pereduksi, sulfur dan karburasi. Penggetasan fase sigma pada suhu 600 hingga 900 °C. Aplikasi untuk bagian tungku perlakuan panas, peralatan pirolisis, da
Baja tahan mulur tinggi yang digunakan untuk produksi bejana tekan dan ketel uap dan dalam konstruksi pembangkit listrik tenaga nuklir. Properti Umum Properti Suhu Nilai Kepadatan 20,0 °C 7,93 g/cm³ Mekanik Properti Suhu Nilai Komentar Modulus elastisitas -100.0 °C 206 IP