Baja tahan panas X12CrNi23-13, mat. No 1.4833, tahan di udara hingga 1000 °C (suhu aplikasi tertinggi). Resistensi rendah terhadap gas belerang (mengurangi serta mengoksidasi). Berarti ketahanan terhadap nitrogen, gas kekurangan oksigen dan karburisasi. Bahan ini ideal untuk pengelasan menurut semua metode pengelasan dan diterapkan dalam konstruksi tungku industri.
Umum
| Properti | Suhu | Nilai |
|---|---|---|
| Kepadatan | 20,0 °C | 7,77 - 7,9 g/cm³ |
Mekanik
| Properti | Suhu | Nilai |
|---|---|---|
| Modulus elastisitas | -100.0 °C | 206 IPK |
| 20,0 °C | 196 IPK | |
| 24.0 °C | 193,7 IPK | |
| 100.0 °C | 190 IPK | |
| 200,0 °C | IPK 182 | |
| 300,0 °C | 174 IPK | |
| 400,0 °C | 166 IPK | |
| 500,0 °C | 158 IPK | |
| 600,0 °C | 150 IPK | |
| 700.0 °C | 142 IPK | |
| 800,0 °C | 134 IPK | |
| 900,0 °C | 127 IPK | |
| 1000.0 °C | 120 IPK | |
| Perpanjangan | 20,0 °C | 35% |
| Perpanjangan A80 | 20,0 °C | 33% |
| Kekerasan, Brinell | 20,0 °C | 192 [-] |
| Rasio Poisson | 24.0 °C | 0,23 - 0,24 [-] |
| Modulus geser | 24.0 °C | 74.5 - 77.9 IPK |
| Kekuatan tarik | 20,0 °C | 500 - 700 MPa |
| Kekuatan hasil Rp0.2 | 20,0 °C | 210 MPa |
| Kekuatan hasil Rp1.0 | 20,0 °C | 250 MPa |
Termal
| Properti | Suhu | Nilai | Komentar |
|---|---|---|---|
| Koefisien ekspansi termal | -100.0 °C | 1.49E-5 1/K | |
| 20,0 °C | 1.61E-5 1/K | ||
| 100.0 °C | 1.67E-5 1/K | ||
| 200,0 °C | 1.6E-5 - 1.72E-5 1/K | ||
| 300,0 °C | 1.77E-5 1/K | ||
| 400,0 °C | 1.75E-5 - 1.81E-5 1/K | ||
| 500,0 °C | 1.84E-5 1/K | ||
| 600,0 °C | 1.8E-5 - 1.88E-5 1/K | ||
| 700.0 °C | 1.91E-5 1/K | ||
| 800,0 °C | 1.85E-5 - 1.94E-5 1/K | ||
| 900,0 °C | 1.97E-5 1/K | ||
| 1000.0 °C | 1.95E-5 - 2E-5 1/K | ||
| Suhu layanan maksimum, lama | 0 - 1000 °C | ||
| Titik leleh | 1230 - 1480 °C | Khas untuk Baja Tahan Karat Austenitik | |
| Kapasitas panas spesifik | -100.0 °C | 440 J/(kg·K) | |
| 20,0 °C | 472 - 500 J/(kg·K) | ||
| 100.0 °C | 487 J/(kg·K) | ||
| 200,0 °C | 503 J/(kg·K) | ||
| 300,0 °C | 512 J/(kg·K) | ||
| 400,0 °C | 520 J/(kg·K) | ||
| 500,0 °C | 530 J/(kg·K) | ||
| 600,0 °C | 541 J/(kg·K) | ||
| 700.0 °C | 551 J/(kg·K) | ||
| 800,0 °C | 559 J/(kg·K) | ||
| 900,0 °C | 565 J/(kg·K) | ||
| 1000.0 °C | 571 J/(kg·K) | ||
| Konduktivitas termal | 20,0 °C | 12,6 - 15 W/(m·K) | |
| 100.0 °C | 14.1 W/(m·K) | ||
| 200,0 °C | 15,9 W/(m·K) | ||
| 300,0 °C | 17,4 W/(m·K) | ||
| 400,0 °C | 19 W/(m·K) | ||
| 500,0 °C | 19 - 20,5 W/(m·K) | ||
| 600,0 °C | 21,9 W/(m·K) | ||
| 700.0 °C | 23.3 W/(m·K) | ||
| 800,0 °C | 24,7 W/(m·K) | ||
| 900,0 °C | 26.1 W/(m·K) | ||
| 1000.0 °C | 27,5 W/(m·K) | ||
| Difusivitas termal | 20,0 °C | 3,4 mm²/s | |
| 100.0 °C | 3,6 mm²/dtk | ||
| 200,0 °C | 3,9 mm²/dtk | ||
| 300,0 °C | 4,3 mm²/s | ||
| 400,0 °C | 4,5 mm²/dtk | ||
| 500,0 °C | 4,7 mm²/s | ||
| 600,0 °C | 4,8 mm²/s | ||
| 700.0 °C | 5,1 mm²/s | ||
| 800,0 °C | 5,5 mm²/dtk | ||
| 900,0 °C | 5,8 mm²/s | ||
| 1000.0 °C | 5,9 mm²/s | ||
Listrik
| Properti | Suhu | Nilai |
|---|---|---|
| Resistivitas listrik | 20,0 °C | 7.8E-7 - 8.68E-7 ·m |
| 100.0 °C | 9.21E-7 ·m | |
| 200,0 °C | 9.75E-7 ·m | |
| 300,0 °C | 1.03E-6 ·m | |
| 400,0 °C | 1.08E-6 ·m | |
| 500,0 °C | 1.12E-6 ·m | |
| 600,0 °C | 1.15E-6 ·m | |
| 700.0 °C | 1.18E-6 ·m | |
| 800,0 °C | 1.21E-6 ·m | |
| 900,0 °C | 1.24E-6 ·m | |
| 1000.0 °C | 1.26E-6 ·m | |
Sifat kimia
| Properti | Nilai |
|---|---|
| Karbon | 0,15% |
| Kromium | 22 - 24% |
| Mangan | 2% |
| Nikel | 12 - 14% |
| Nitrogen | 0,11 % |
| Fosfor | 0,05% |
| Silikon | 1% |
| Belerang | 0,015% |
Logam
Baja tahan panas austenitik X15CrNiSi20-12, mat. No 1.4828 menunjukkan resistensi penskalaan tinggi hingga maks. 1000 °C (suhu aplikasi tertinggi di udara). Baja memiliki ketahanan yang tinggi terhadap oksidasi athmosphere. Aplikasi untuk komponen oven, ban berjalan dan kotak sisipan serta dalam tek
Aplikasi untuk bagian dalam tungku industri, ketel uap, pabrik minyak bumi, untuk tabung selubung termometer. Resistensi terbaik terhadap nitrogen, gas kekurangan oksigen. Tahan panas di udara hingga 1050 °C.(suhu aplikasi tertinggi). Properti Umum Properti Suhu Nilai Kepadatan 20,0 °C 7
X15CrNiSi25-20 menunjukkan ketahanan penskalaan hingga maks. 1150 °C (suhu aplikasi tertinggi di udara). Baja ini sedikit tahan terhadap atmosfir pereduksi, sulfur dan karburasi. Penggetasan fase sigma pada suhu 600 hingga 900 °C. Aplikasi untuk bagian tungku perlakuan panas, peralatan pirolisis, da
Baja tahan panas X12CrNi23-13, mat. No 1.4833, tahan di udara hingga 1000 °C (suhu aplikasi tertinggi). Resistensi rendah terhadap gas belerang (mengurangi serta mengoksidasi). Berarti ketahanan terhadap nitrogen, gas kekurangan oksigen dan karburisasi. Bahan ini ideal untuk pengelasan menurut semua