Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,705 g/cm³ | H16 | Standar AA, ASTM B209, ASTM B211 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 45,0 MPa | H16 | Standar AA | |
| Modulus elastisitas | 69.0 IPK | H16 | Standar AA, ASTM B209, ASTM B211 | |
| Kekerasan, Brinell | 30.0 [-] | H16 | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 1000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 1000 Tempa | ||
| Modulus geser | 25.9 IPK | Khas untuk Aluminium Seri 1000 Tempa | ||
| Kekuatan tarik | 95.0 - 130.0 MPa | H16 | Standar AA, ASTM B209 | |
| 110,0 MPa | H16 | Standar AA, ASTM B211 | ||
| 115,0 MPa | H16 | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.36e-05 1/K | H16 | Standar AA, ASTM B209, ASTM B211 | |
| 100 °C | 2.36e-05 1/K | H16 | Standar AA, ASTM B209, ASTM B211 | ||
| Titik leleh | 645.0 - 655.0 °C | H16 | Standar AA, ASTM B209, ASTM B211 | ||
| Kapasitas panas spesifik | 900,0 - 963,0 J/(kg·K) | Khas untuk Aluminium Seri 1000 Tempa | |||
| Konduktivitas termal | 230.0 - 234.0 W/(m·K) | H16 | Standar AA, ASTM B209, ASTM B211 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 35000000.0 - 36000000.0 S/m | H16 | Standar AA, ASTM B209, ASTM B211 |
| Resistivitas listrik | 2.78-08 - 2.86-08 ·m | H16 | Standar AA, ASTM B209, ASTM B211 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Aluminium | 99,6% | H16 | Standar AA, ASTM B209, ASTM B211 |
| Tembaga | 0,05% | H16 | Standar AA, ASTM B209, ASTM B211 |
| Besi | 0,35% | H16 | Standar AA, ASTM B209, ASTM B211 |
| Magnesium | 0,03 % | H16 | Standar AA, ASTM B209, ASTM B211 |
| Mangan | 0,03 % | H16 | Standar AA, ASTM B209, ASTM B211 |
| Silikon | 0,25% | H16 | Standar AA, ASTM B209, ASTM B211 |
| Titanium | 0,03 % | H16 | Standar AA, ASTM B209, ASTM B211 |
| Vanadium | 0,05% | H16 | Standar AA, ASTM B209, ASTM B211 |
| Seng | 0,05% | H16 | Standar AA, ASTM B209, ASTM B211 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:mungkin dengan proses dan metode komersial
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:tidak sesuai (O, H12), buruk (H14, H16, H18)
| |
| Kemampuan Kerja | umum (kondisi):baik (O, H12, H14), dapat diterima (H16, H18)
| |
Logam
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,705 g/cm³ H14 Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 35,0 MPa H14 Standar AA Modulu
Aluminium AA 5005 adalah paduan magnesium aluminium ramping dengan kepadatan rendah dan konduktivitas termal yang sangat baik. Paduan non-panas yang tidak dapat diolah dengan kekuatan sedang ini dikenal karena ketahanannya terhadap korosi dalam situasi laut alkali. Aluminium AA 5005 mudah dikerjakan
Aluminium AA 3003 adalah paduan populer yang menawarkan ketahanan korosi atmosferik yang sangat baik kepada pelanggan dan kekuatan sedang. Aluminium 3003 menawarkan kemampuan mesin yang baik untuk paduan aluminium, meskipun tidak dapat diolah dengan panas. Tidak seperti paduan aluminium lainnya, AA
AA 1100 adalah paduan yang lembut, tidak dapat diolah dengan panas, dan berkekuatan rendah yang menawarkan ketahanan korosi yang kuat. Terdiri dari 99% aluminium dan 0,12% tembaga, AA 1100 adalah paduan aluminium kelas paling murni yang tersedia secara komersial. Properti Umum Properti Nila