EN 10272 Grade X2CrNiMoN17-13-5 solusi anil (+AT)

-100.0 °C

206 IPK

20,0 °C

196 - 200 IPK

100.0 °C

190 - 194 IPK

200,0 °C

182 - 186 IPK

300,0 °C

174 - 179 IPK

400,0 °C

166 - 172 IPK

500,0 °C

158 - 165 IPK

600,0 °C

150 IPK

700.0 °C

142 IPK

800,0 °C

134 IPK

20,0 °C

580 - 800 MPa

100.0 °C

520 MPa

150,0 °C

490 MPa

200,0 °C

460 MPa

250,0 °C

450 MPa

300,0 °C

440 MPa

350,0 °C

435 MPa

20,0 °C

280 MPa

100.0 °C

225 MPa

150,0 °C

200 MPa

200,0 °C

185 MPa

250,0 °C

175 MPa

300,0 °C

165 MPa

350,0 °C

155 MPa

400,0 °C

150 MPa

20,0 °C

315 MPa

100.0 °C

255 MPa

150,0 °C

230 MPa

200,0 °C

210 MPa

250,0 °C

200 MPa

300,0 °C

190 MPa

350,0 °C

180 MPa

400,0 °C

175 MPa

-100.0 °C

1.49E-5 1/K

20,0 °C

1.61E-5 1/K

100.0 °C

1.6E-5 - 1.67E-5 1/K

200,0 °C

1.65E-5 - 1.72E-5 1/K

300,0 °C

1.7E-5 - 1.77E-5 1/K

400,0 °C

1.75E-5 - 1.81E-5 1/K

500,0 °C

1.8E-5 - 1.84E-5 1/K

600,0 °C

1.88E-5 1/K

700.0 °C

1.91E-5 1/K

800,0 °C

1.94E-5 1/K

900,0 °C

1.97E-5 1/K

1000.0 °C

2E-5 1/K

-100.0 °C

440 J/(kg·K)

20,0 °C

472 - 500 J/(kg·K)

100.0 °C

487 J/(kg·K)

200,0 °C

503 J/(kg·K)

300,0 °C

512 J/(kg·K)

400,0 °C

520 J/(kg·K)

500,0 °C

530 J/(kg·K)

600,0 °C

541 J/(kg·K)

700.0 °C

551 J/(kg·K)

800,0 °C

559 J/(kg·K)

900,0 °C

565 J/(kg·K)

1000.0 °C

571 J/(kg·K)

20,0 °C

13,5 - 14 W/(m·K)

100.0 °C

14,9 W/(m·K)

200,0 °C

16,7 W/(m·K)

300,0 °C

18,3 W/(m·K)

400,0 °C

19,8 W/(m·K)

500,0 °C

21,3 W/(m·K)

600,0 °C

22,7 W/(m·K)

700.0 °C

24,2 W/(m·K)

800,0 °C

25,6 W/(m·K)

20,0 °C

3,6 mm²/dtk

100.0 °C

3,7 mm²/s

200,0 °C

4 mm²/s

300,0 °C

4,4 mm²/dtk

400,0 °C

4,6 mm²/s

500,0 °C

4,7 mm²/s

600,0 °C

4,9 mm²/dtk

700.0 °C

5,2 mm²/s

800,0 °C

5,5 mm²/dtk