Logam
Manufaktur industri
Bahan cor yang dapat dilas dengan baik dengan sifat pengecoran yang baik. Pengecoran peka terhadap beban benturan.Aplikasi:fitting
Kepadatan
2,7 g/cm³
T6
WL 3.2134
Transmisi
20,0 °C
2,7 g/cm³
T6
WL 3.2134
Mekanik
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk | Komentar |
|---|---|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 60,0 MPa | T6 | WL 3.2134 | Transmisi | ||
| 70.0 MPa | T6 | WL 3.2134 | Transmisi | |||
| Modulus elastisitas | 71.0 IPK | T6 | WL 3.2134 | Transmisi | ||
| 20,0 °C | 71.0 IPK | T6 | WL 3.2134 | |||
| Perpanjangan | 0,5% | T6 | WL 3.2134 | Transmisi | A50 | |
| 20,0 °C | 0,5% | T6 | WL 3.2134 | |||
| 20,0 °C | 1,5% | T6 | WL 3.2134 | |||
| 20,0 °C | 2,0% | T6 | WL 3.2134 | |||
| Kekerasan, Brinell | 75.0 [-] | T6 | WL 3.2134 | Transmisi | ||
| 20,0 °C | 75.0 [-] | T6 | WL 3.2134 | |||
| 20,0 °C | 80.0 [-] | T6 | WL 3.2134 | |||
| 20,0 °C | 85.0 [-] | T6 | WL 3.2134 | |||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Cast 3xx.x Series | ||||
| Modulus geser | 2.8 IPK | Khas untuk Aluminium Cast 3xx.x Series | ||||
| Kekuatan geser | 20,0 °C | 190.0 MPa | T6 | WL 3.2134 | ||
| 20,0 °C | 210.0 MPa | T6 | WL 3.2134 | |||
| Kekuatan tarik | 190.0 MPa | T6 | WL 3.2134 | Transmisi | ||
| 20,0 °C | 190.0 MPa | T6 | WL 3.2134 | |||
| 20,0 °C | 200,0 MPa | T6 | WL 3.2134 | |||
| 20,0 °C | 210.0 MPa | T6 | WL 3.2134 | |||
| 20,0 °C | 220.0 MPa | T6 | WL 3.2134 | |||
| 20,0 °C | 250,0 MPa | T6 | WL 3.2134 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk | Komentar |
|---|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.2e-05 1/K | T6 | WL 3.2134 | Transmisi | |
| 100 °C | 2.2e-05 1/K | T6 | WL 3.2134 | Transmisi | ||
| Titik leleh | 545,0 - 621,0 °C | T6 | WL 3.2134 | Transmisi | ||
| Kapasitas panas spesifik | 960.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Cast 3xx.x Series | ||||
| Konduktivitas termal | 142,0 - 176.0 W/(m·K) | T6 | WL 3.2134 | Transmisi |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|
| Konduktivitas listrik | 19000000.0 - 25000000.0 S/m | T6 | WL 3.2134 | Transmisi |
| Resistivitas listrik | 4e-08 - 5.26e-08 ·m | T6 | WL 3.2134 | Transmisi |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|
| Kromium | 0,25% | T6 | WL 3.2134 | Transmisi |
| Tembaga | 1,0 - 1,5% | T6 | WL 3.2134 | Transmisi |
| Besi | 0,6% | T6 | WL 3.2134 | |
| 0,60% | T6 | WL 3.2134 | Transmisi | |
| Magnesium | 0,4 - 0,6% | T6 | WL 3.2134 | Transmisi |
| Mangan | 0,5% | T6 | WL 3.2134 | Transmisi |
| Silikon | 4,5 - 5,5% | T6 | WL 3.2134 | Transmisi |
| Titanium | 0,25% | T6 | WL 3.2134 | Transmisi |
| Seng | 0,3% | T6 | WL 3.2134 | Transmisi |
Properti teknologi
| Properti | ||
|---|---|---|
| Metode pemrosesan | pengecoran cetakan permanen
| |
Logam
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan
Paduan pengecoran aluminium (pengecoran cetakan permanen) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan Membungkuk 70.0 -
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan Membungkuk
Paduan pengecoran aluminium (tekanan die casting) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,75 g/cm³ F EN 1706 Transmisi 20,0 °C 2,75 g/cm³ F EN 1706 Mekanik Properti Suhu Nilai Kondisi Standar T