| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,66 g/cm³ | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 125,0 MPa | H32 | Standar AA | |
| Modulus elastisitas | 70.0 IPK | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | |
| Kekerasan, Brinell | 67.0 [-] | H32 | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 5000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 5000 Tempa | ||
| Modulus geser | 26.0 - 26.5 IPK | Khas untuk Aluminium Seri 5000 Tempa | ||
| Kekuatan tarik | 250.0 - 300,0 MPa | H32 | Standar AA, ASTM B209, ASTM B313, ASTM B547 | |
| 250,0 MPa | H32 | Standar AA, ASTM B211 | ||
| 270,0 MPa | H32 | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.3899999999999998e-05 1/K | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | |
| 100 °C | 2.3899999999999998e-05 1/K | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | ||
| Suhu layanan maksimum | 150,0 °C | Khas untuk Aluminium Seri 5000 Tempa | |||
| Titik leleh | 590.0 - 645.0 °C | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 | ||
| Kapasitas panas spesifik | 879.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Seri 5000 Tempa | |||
| Konduktivitas termal | 126 W/(m·K) | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 19000000.0 S/m | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Resistivitas listrik | 5.26e-08 ·m | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kromium | 0,15 - 0,35 % | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Tembaga | 0,1% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Besi | 0,40% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Magnesium | 3,1 - 3,9% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Mangan | 0,1% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Silikon | 0,25% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Titanium | 0,2% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
| Seng | 0,2% | H32 | Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:tidak ada pematrian yang diketahui atau dikembangkan
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:kurang (O, H32), cukup (H34, H36, H38)
| |
| Kemampuan Kerja | umum (kondisi):baik (O), dapat diterima (H32, H34), buruk (H36, H38)
| |
Logam
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,66 g/cm³ H32 Standar AA, ASTM B209, ASTM B211, ASTM B313, ASTM B547 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 125,0 MPa H32 Standar AA Modulus elastisit
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,66 g/cm³ O Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 115,0 MPa O Standar AA
Aluminium AA 5086 adalah paduan struktural, yang menawarkan ketahanan korosi yang kuat kepada pengguna dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat dengan pengerasan noda dan pengerjaan dingin, sambil tetap menja
Aluminium AA 5052 adalah paduan non-panas yang dapat diolah dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang pal