Legam Aluminium AA 5086 H32 – Kekuatan Premium & Ketahanan Korosi untuk Aplikasi Struktural

Legam aluminium AA 5086 adalah struktural yang menawarkan ketahanan korosi yang kuat dan konduktivitas listrik tinggi. Dengan tingkat kekuatan yang lebih tinggi dibandingkan 5052 atau 5083, AA 5086 menjadi lebih kuat melalui pengeringan stain dan kerja dingin, sambil tetap menjadi pilihan yang hemat biaya. Legam ini dapat dielas dengan metode konvensional, meskipun pengelasan busa listrik disarankan.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Masa jenis	2.66 g/cm³	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Mekanis

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Modulus elastis	71.0 GPa	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Kekuatan retakan fraktur tekanan bidang	22.0 - 35.0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Rasio Poisson	0.33 [-]			Typical for Wrought 5000 Series Aluminium
Modulus geser	26.0 - 26.5 GPa			Typical for Wrought 5000 Series Aluminium
Kekuatan tarik	275.0 - 325.0 MPa	H32	Standar AA, ASTM B209, ASTM B313, ASTM B547
Kekuatan tarik	275.0 MPa	H32	Standar AA, ASTM B210
Kekuatan tarik	290.0 MPa	H32	Standar AA

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien ekspansi termal	20 °C	2.38e-05 1/K	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Koefisien ekspansi termal	100 °C	2.38e-05 1/K	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Suhu operasional maksimum		150.0 °C			Typical for Wrought 5000 Series Aluminium
Titik leleh		585.0 - 640.0 °C	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Kapasitas panas spesifik		879.0 - 963.0 J/(kg·K)			Typical for Wrought 5000 Series Aluminium
Konduktivitas termal		126 W/(m·K)	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas listrik	18.000.000,0 S/m	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Resistivitas listrik	5.56e-08 Ω·m	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Kimia

Properti	Nilai	Kondisi	Standar Terkait
Kromium	0.05 - 0.25 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Tembaga	0.1 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Besi	0.50 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Magnesium	3.5 - 4.5 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Mangan	0.2 - 0.7 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Silikon	0.4 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Titanium	0.15 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Seng	0.25 %	H32	Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Teknologis

Properti	Keterangan
Brazing	Secara umum: tidak ada brazing yang diketahui atau dikembangkan
Sifat korosi	Retakan korosi tegangan: tidak ada kerusakan selama operasi dan uji laboratorium (O, H32, H116, H111), tidak ada kerusakan selama operasi, kerusakan terbatas selama uji laboratorium (H34, H36, H38), secara umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Keolahan mesin umum	Secara umum: buruk (O, H32, H116, H111), cukup (H34, H36, H38)
Kekrajaan	Secara umum (kondisi): baik (O), dapat diterima (H32, H116, H111), buruk (H36, H38)