Maksimalkan Kinerja: JIS G4311 SUH38 Grade Penuaan Setelah Treatment Larutan

Properti

Umum

Properti	Suhu	Nilai	Keterangan
Density	23.0 °C	7.9 - 8.2 g/cm³	Typical for Austenitic Stainless Steel

Mekanis

Properti	Suhu	Nilai	Keterangan
Elastic modulus	23.0 °C	195 GPa	Typical for Austenitic Stainless Steel
Elongation A5	23.0 °C	20 %
Hardness, Brinell	23.0 °C	269 [-]
Poisson's ratio	23.0 °C	0.3 [-]	Typical for Austenitic Stainless Steel
Reduction of area	23.0 °C	25 %
Shear modulus	23.0 °C	77 GPa	Typical for Austenitic Stainless Steel
Tensile strength	23.0 °C	880 MPa
Yield strength Rp0.2	23.0 °C	490 MPa

Termal

Properti	Suhu	Nilai	Keterangan
Coefficient of thermal expansion	23.0 °C	1.7E-5 - 1.9E-5 1/K	Typical for Austenitic Stainless Steel
Melting point		1230 - 1480 °C	Typical for Austenitic Stainless Steel
Specific heat capacity	23.0 °C	440 J/(kg·K)	Typical for Austenitic Stainless Steel
Thermal conductivity	23.0 °C	11 - 21 W/(m·K)	Typical for Austenitic Stainless Steel

Listrik

Properti	Suhu	Nilai	Keterangan
Electrical resistivity	23.0 °C	8.5E-7 Ω·m	Typical for Austenitic Stainless Steel

Properti Teknologis

Properti
Processing history	ageing treatment after solution treatment