Baja ASTM A709 Grade 250: Sifat Utama & Spesifikasi

Properti

Umum

Properti	Suhu	Nilai	Keterangan
Kepadatan	23.0 °C	7.8 - 7.9 g/cm³	Typical for Low Carbon Steel

Mekanis

Properti	Suhu	Nilai	Keterangan
Modulus elastisitas	23.0 °C	200 - 215 GPa	Typical for Low Carbon Steel
Elongasi A50	23.0 °C	23 %
Rasio Poisson	23.0 °C	0.29 [-]	Typical for Low Carbon Steel
Modulus geser	23.0 °C	82 GPa	Typical for Low Carbon Steel
Kekuatan tarik	23.0 °C	400 - 550 MPa
Kekuatan leleh Rp0.2	23.0 °C	250 MPa

Termal

Properti	Suhu	Nilai	Keterangan
Koefisien ekspansi termal	23.0 °C	1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Suhu operasi maksimal		500 °C	Typical for Carbon Steel
Titik leleh		1480 - 1526 °C	Typical for Low Carbon Steel
Kalor jenis	23.0 °C	465 J/(kg·K)	Typical for Low Carbon Steel
Konduktivitas termal	23.0 °C	25 - 93 W/(m·K)	Typical for Low Carbon Steel

Listrik

Properti	Suhu	Nilai	Keterangan
Resistivitas listrik	23.0 °C	1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Magnetik

Properti	Nilai	Keterangan
Suhu Curie	770 °C	Typical for Low Carbon Steel

Sifat Kimia

Properti	Nilai
Karbon	0.26 %
Tembaga	0.2 %
Fosfor	0.04 %
Silikon	0.4 %
Sulfur	0.05 %