DIN 17155 Grade 13CrMo4-4 Baja Dipanaskan & Dipanaskan Kembali: Performa Suhu Tinggi

Baja suhu tinggi hingga 530 °C untuk aplikasi berikut: konstruksi tabung untuk superheater dan tabung uap panas, kolektor, flange, konstruksi apparatus, dan industri petrokimia.

Properti

Umum

Properti	Suhu	Nilai
Kepadatan	20.0 °C	7.85 g/cm³
	50.0 °C	7.84 g/cm³
	100.0 °C	7.82 g/cm³
	150.0 °C	7.81 g/cm³
	200.0 °C	7.79 g/cm³
	250.0 °C	7.77 g/cm³
	300.0 °C	7.76 g/cm³
	350.0 °C	7.74 g/cm³
	400.0 °C	7.72 g/cm³
	450.0 °C	7.7 g/cm³
	500.0 °C	7.68 g/cm³
	550.0 °C	7.66 g/cm³
	600.0 °C	7.64 g/cm³

Mekanis

Properti	Suhu	Nilai
Modulus elastisitas	-100.0 °C	217 GPa
	20.0 °C	212 – 212.48 GPa
	50.0 °C	211.6 GPa
	100.0 °C	207 – 209 GPa
	150.0 °C	205.52 GPa
	200.0 °C	199 – 202 GPa
	250.0 °C	197.67 GPa
	300.0 °C	192 – 193.45 GPa
	350.0 °C	189.23 GPa
	400.0 °C	184 – 185 GPa
	450.0 °C	180.41 GPa
	500.0 °C	175 – 176 GPa
	550.0 °C	171.28 GPa
	600.0 °C	164 – 166.57 GPa
Regangan	20.0 °C	18 – 20 %
Rasio Poisson	20.0 °C	0.28 [-]
	50.0 °C	0.28 [-]
	100.0 °C	0.28 [-]
	150.0 °C	0.29 [-]
	200.0 °C	0.29 [-]
	250.0 °C	0.29 [-]
	300.0 °C	0.29 [-]
	350.0 °C	0.3 [-]
	400.0 °C	0.3 [-]
	450.0 °C	0.3 [-]
	500.0 °C	0.3 [-]
	550.0 °C	0.31 [-]
	600.0 °C	0.31 [-]
Modulus geser	20.0 °C	82.8 GPa
	50.0 °C	82.4 GPa
	100.0 °C	81.42 GPa
	150.0 °C	79.95 GPa
	200.0 °C	78.38 GPa
	250.0 °C	76.62 GPa
	300.0 °C	74.85 GPa
	350.0 °C	73.08 GPa
	400.0 °C	71.32 GPa
	450.0 °C	69.45 GPa
	500.0 °C	67.59 GPa
	550.0 °C	65.63 GPa
	600.0 °C	63.57 GPa
Kekuatan tarik	20.0 °C	420 – 600 MPa
	200.0 °C	390 MPa
	250.0 °C	390 MPa
	300.0 °C	390 MPa
	350.0 °C	390 MPa
	400.0 °C	385 MPa
	450.0 °C	365 MPa
	500.0 °C	335 MPa
Kekuatan leleh Rp0.2	20.0 °C	240 – 300 MPa
	100.0 °C	220 – 260 MPa
	150.0 °C	210 – 245 MPa
	200.0 °C	200 – 255 MPa
	250.0 °C	190 – 245 MPa
	300.0 °C	175 – 230 MPa
	350.0 °C	165 – 215 MPa
	400.0 °C	160 – 205 MPa
	450.0 °C	150 – 195 MPa
	500.0 °C	145 – 190 MPa

Termal

Properti	Suhu	Nilai	Keterangan
Koefisien ekspansi termal	-100.0 °C	1.05E-5 1/K
	20.0 °C	1.15E-5 1/K
	100.0 °C	1.21E-5 – 1.22E-5 1/K
	200.0 °C	1.27E-5 – 1.29E-5 1/K
	300.0 °C	1.32E-5 – 1.34E-5 1/K
	400.0 °C	1.36E-5 – 1.4E-5 1/K
	500.0 °C	1.4E-5 – 1.43E-5 1/K
	600.0 °C	1.44E-5 – 1.46E-5 1/K
Suhu operasi maksimal, jangka panjang		0 – 530 °C
Titik leleh		1382 – 1529 °C	Typikal untuk baja kromium molibdenum
Kapasitas kalor jenis	-100.0 °C	423 J/(kg·K)
	20.0 °C	461 J/(kg·K)
	100.0 °C	479 – 500 J/(kg·K)
	200.0 °C	499 – 540 J/(kg·K)
	300.0 °C	517 – 580 J/(kg·K)
	400.0 °C	536 – 620 J/(kg·K)
	500.0 °C	558 – 690 J/(kg·K)
	600.0 °C	587 – 780 J/(kg·K)
Konduktivitas termal	20.0 °C	45.9 W/(m·K)
	100.0 °C	46 – 46.4 W/(m·K)
	200.0 °C	45.6 – 46 W/(m·K)
	300.0 °C	43 – 43.5 W/(m·K)
	400.0 °C	40.9 – 41 W/(m·K)
	500.0 °C	38 – 38.2 W/(m·K)
	600.0 °C	35.5 – 36 W/(m·K)
Difusivitas termal	20.0 °C	12.7 mm²/s
	100.0 °C	12 mm²/s
	200.0 °C	11 mm²/s
	300.0 °C	9.9 mm²/s
	400.0 °C	8.7 mm²/s
	500.0 °C	7.3 mm²/s
	600.0 °C	6 mm²/s

Listrik

Properti	Suhu	Nilai
Resistivitas listrik	20.0 °C	2.27E-7 – 2.37E-7 Ω·m
	50.0 °C	2.56E-7 Ω·m
	100.0 °C	2.76E-7 – 2.88E-7 Ω·m
	150.0 °C	3.21E-7 Ω·m
	200.0 °C	3.46E-7 – 3.59E-7 Ω·m
	250.0 °C	4.01E-7 Ω·m
	300.0 °C	4.3E-7 – 4.45E-7 Ω·m
	350.0 °C	4.95E-7 Ω·m
	400.0 °C	5.3E-7 – 5.48E-7 Ω·m
	450.0 °C	6.06E-7 Ω·m
	500.0 °C	6.48E-7 – 6.63E-7 Ω·m
	550.0 °C	7.28E-7 Ω·m
	600.0 °C	7.8E-7 – 7.97E-7 Ω·m

Properti Kimia

Properti	Nilai
Karbon	0.08 – 0.18 %
Kromium	0.7 – 1.15 %
Mangan	0.4 – 1 %
Molibdenum	0.4 – 0.8 %
Fosfor	0.04 %
Silikon	0.1 – 0.4 %
Sulfur	0.03 %

DIN 17240 Grade C35 Baja – Normalisasi atau Bentuk Normalisasi (+N) untuk Ketahanan Creep hingga 400 °C DIN 17245 G‑X8CrNi12: Baja Dipanaskan & Dipanaskan Kembali untuk Air & Uap hingga 400 °C

Logam