Logam
Manufaktur industri
Kepadatan
3,1 g/cm³
T6
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Bentuk | Komentar |
|---|---|---|---|---|---|
| Energi benturan Charpy, V-notch | 5.0 - 15.0 J | T6 | |||
| Modulus elastisitas | 71.0 IPK | T6 | |||
| 71 IPK | T6 | ||||
| Perpanjangan | 4,0% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi | A100 |
| 7,2% | T6 | ||||
| 8% | T6 | Cetakan pasir, pemanjangan dalam 50 mm | |||
| Kekerasan, Brinell | 135 [-] | T6 | Beban 500 kg, 10 mm b | ||
| Rasio Poisson | 0.33 [-] | T6 | |||
| Modulus geser | IPK 23.0 | T6 | |||
| Kekuatan tarik | 415,0 MPa | T6 | Seprai Merah Muda, ASTM B618 | Transmisi | |
| 448 MPa | T6 | Cetakan pasir | |||
| 460.0 MPa | T6 | ||||
| Kekuatan hasil | 345.0 MPa | T6 | Seprai Merah Muda, ASTM B618 | Transmisi | Rp02 |
| 379 MPa | T6 | Cetakan pasir, RP02 | |||
| 400,0 MPa | T6 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk | Komentar |
|---|---|---|---|---|---|---|
| Koefisien ekspansi termal | 2.1e-05 1/K | T6 | ||||
| 100 °C | 0,0000193 1/K | T6 | nilai yang tidak disebutkan antara 20°C dan suhu yang disebutkan | |||
| 200 °C | 0,0000227 1/K | T6 | nilai yang tidak disebutkan antara 20°C dan suhu yang disebutkan | |||
| 300 °C | 0,0000247 1/K | T6 | nilai yang tidak disebutkan antara 20°C dan suhu yang disebutkan | |||
| Titik leleh | 570.0 °C | T6 | ||||
| 571.0 - 649.0 °C | T6 | Seprai Merah Muda, ASTM B618 | Transmisi | |||
| Kapasitas panas spesifik | 920,0 J/(kg·K) | T6 | ||||
| Konduktivitas termal | 120,0 W/(m·K) | T6 |
Listrik
| Properti | Nilai | Kondisi | Komentar |
|---|---|---|---|
| Konduktivitas listrik | 16000000.0 - 19000000.0 S/m | T6 | Nilai Khas/Turunan |
| Resistivitas listrik | 5.4e-08 - 6.4e-08 ·m | T6 | Nilai umum |
| Konduktivitas Listrik Spesifik | 27.0 - 32,0% IACS | T6 | Nilai umum |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|
| Aluminium | 92.1 - 95.1% | T6 | ||
| Tembaga | 4.0 - 5.2% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
| Besi | 0,15% | T6 | ||
| 0,15% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi | |
| Magnesium | 0,15 - 0,55 % | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
| Mangan | 0,2 - 0,5% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
| Lainnya | 0,1% | T6 | ||
| Silikon | 0,1% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
| Perak | 0,4 - 1,0% | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
| Titanium | 0,15 - 0,35 % | T6 | Seprai Merah Muda, ASTM B618 | Transmisi |
Logam
Properti Umum Properti Nilai Kondisi Kepadatan 2,7 g/cm³ T6 Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan luluh tekan 172.0 - 186.0 MPa T6 Modulus elastisitas 72.0 IPK T6 72.4 IPK T6 Perpanjangan -195 °C
Properti Umum Properti Nilai Kondisi Kepadatan 3,0 g/cm³ F Mekanik Properti Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan luluh tekan 131 MPa F Modulus elastisitas 74 IPK F 78.0 IPK F Perpanjangan 1,5% F Seprai Merah Muda,
Properti Umum Properti Nilai Kondisi Kepadatan 2,7 g/cm³ T7 Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan luluh tekan 165.0 - 214.0 MPa T7 Modulus elastisitas 72.0 IPK T7 72.4 IPK T7 Perpanjangan -195 °C
Bahan cor yang dapat dilas sangat baik dengan sifat pengecoran yang sangat baik. Pengecoran sensitif terhadap beban benturan.Aplikasi:fitting Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Kepadatan 20,0 °C 2,7 g/cm³ T5 WL 3.2364 Mekanik Properti Suhu Nilai Kond