DIN 17851 Grade TiAl6V4: Legas Titanium Premium Artificially Aged – Kekuatan dan Keawetan Tinggi

Legas titanium DIN TiAl6V4 adalah legas titanium yang paling banyak tersedia secara komersial di antara semua legas titanium. Legas ini menawarkan kombinasi yang sangat baik antara kekuatan tinggi dan keawetan. Titanium DIN TiAl6V4 memiliki karakteristik las dan fabrikasi yang baik.

Properti

Umum

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Bentuk
Masa jenis	20,0 °C	4,43 g/cm³	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod

Mekanik

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Bentuk
Modul elastisitas	-269,0 °C	119,6 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	-195,0 °C	118,2 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	20,0 °C	110,0 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	27,0 °C	109,2 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	200,0 °C	98,0 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	400,0 °C	84,0 GPa	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Regangan	20,0 °C	8,0 %	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Rod, Forging
Kekerasan, Brinell	20,0 °C	310,0	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Rod
Rasio Poisson	-269,0 °C	0,311 [-]	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	-195,0 °C	0,327 [-]	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
	27,0 °C	0,333 [-]	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Pengurangan luas penampang	20,0 °C	15,0 %	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Rod, Forging
	20,0 °C	20,0 %	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Forging
Modul geser	20,0 °C	43,0 GPa	Artificially Aged	WL 3.7164-1, DIN 17851, DIN 17862, DIN 17864, DIN 17860	Forging, Rod
Kekuatan regangan	20,0 °C	1060,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Forging
	20,0 °C	1070,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Rod, Forging
	20,0 °C	1100,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860	Forging, Rod
	20,0 °C	1180,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860
	100,0 °C	1090,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860
	200,0 °C	1000,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860
	300,0 °C	910,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860
	400,0 °C	855,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860
	500,0 °C	735,0 MPa	Artificially Aged	DIN 17862, WL 3.7164-1, DIN 17851, DIN 17864, DIN 17860

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Bentuk	Keterangan
Koefisien ekspansi termal		7,699999999999999e-06 - 1e-05 1/K				Typical for Titanium Alpha Beta Alloy
Titik leleh		1500,0 - 1750,0 °C				Typical for Titanium Alpha Beta Alloy
Kapasitas panas spesifik		370,0 - 674,0 J/(kg·K)				Typical for Titanium Alpha Beta Alloy
Konduktivitas termal	20,0 °C	7,12 W/(m·K)	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod

Listrik

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Bentuk
Resistivitas listrik	20,0 °C	1,71e-06 Ω·m	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod

Properti kimia

Properti	Nilai	Kondisi	Standar Terkait	Bentuk
Aluminium	5,5 - 6,75 %	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Karbon	0,08	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Hidrogen	0,015	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Besi	0,3	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Nitrogen	0,05	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Oksigen	0,2	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Titanium	87,7 %	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod
Vanadium	3,5 - 4,5 %	Artificially Aged	DIN 17851, DIN 17864, WL 3.7164-1, DIN 17862, DIN 17860	Forging, Rod