EN 10277-5 Grade C50E Baja Tarik Dingin – Kekuatan Tinggi untuk Teknik Berat
Baja C50E cocok untuk bagian besar (bagian tempa berat) dalam teknik kendaraan, mesin, dan mesin (misalnya bagian transmisi, poros, hub roda). Suhu aplikasi terendah -25°C. Sebagai produk baja terang, digunakan dalam bentuk batas, terang, lurus, dalam berbagai kondisi (lihat DIN EN 10277 : 1999-10).
Sifat
Umum
| Sifat | Suhu | Nilai |
|---|
| Kepadatan | 20.0 °C | 7.8 - 7.85 g/cm³ |
Mekanis
| Sifat | Suhu | Nilai | Keterangan |
|---|
| Modulus elastisitas | -100.0 °C | 217 GPa | |
| 20.0 °C | 210 - 212 GPa | |
| 100.0 °C | 205 - 207 GPa | |
| 200.0 °C | 195 - 199 GPa | |
| 300.0 °C | 185 - 192 GPa | |
| 400.0 °C | 175 - 184 GPa | |
| 500.0 °C | 175 GPa | |
| 600.0 °C | 164 GPa | |
| Regangan patah | 20.0 °C | 5 - 8 % | |
| Rasio Poisson | 23.0 °C | 0.29 [-] | Typical for Medium Carbon Steel |
| Modulus geser | 20.0 °C | 81 GPa | |
| Kekuatan regangan | 20.0 °C | 650 - 1100 MPa | |
| Kekuatan leleh Rp0.2 | 20.0 °C | 390 - 590 MPa | |
Termal
| Sifat | Suhu | Nilai | Keterangan |
|---|
| Koefisien pembesaran termal | -100.0 °C | 1.08E-5 1/K | |
| 20.0 °C | 1.19E-5 1/K | |
| 100.0 °C | 1.11E-5 - 1.25E-5 1/K | |
| 200.0 °C | 1.21E-5 - 1.3E-5 1/K | |
| 300.0 °C | 1.29E-5 - 1.36E-5 1/K | |
| 400.0 °C | 1.35E-5 - 1.41E-5 1/K | |
| 500.0 °C | 1.45E-5 1/K | |
| 600.0 °C | 1.49E-5 1/K | |
| Suhu layanan maksimal | | 500 °C | Typical for Carbon Steel |
| Suhu layanan maksimal, jangka panjang | | -25 - 0 °C | |
| Titik leleh | | 1380 - 1514 °C | Typical for Medium Carbon Steel |
| Kalor jenis | -100.0 °C | 423 J/(kg·K) | |
| 20.0 °C | 460 - 461 J/(kg·K) | |
| 100.0 °C | 479 J/(kg·K) | |
| 200.0 °C | 499 J/(kg·K) | |
| 300.0 °C | 517 J/(kg·K) | |
| 400.0 °C | 536 J/(kg·K) | |
| 500.0 °C | 558 J/(kg·K) | |
| 600.0 °C | 587 J/(kg·K) | |
| Konduktivitas termal | 20.0 °C | 41.7 - 52 W/(m·K) | |
| 100.0 °C | 43.4 - 50.6 W/(m·K) | |
| 200.0 °C | 43.2 - 48.1 W/(m·K) | |
| 300.0 °C | 41.4 - 45.7 W/(m·K) | |
| 400.0 °C | 39.1 W/(m·K) | |
| 500.0 °C | 36.7 W/(m·K) | |
| 600.0 °C | 34.1 W/(m·K) | |
| Difusivitas termal | 20.0 °C | 11.6 mm²/s | |
| 100.0 °C | 11.3 mm²/s | |
| 200.0 °C | 10.5 mm²/s | |
| 300.0 °C | 9.5 mm²/s | |
| 400.0 °C | 8.3 mm²/s | |
| 500.0 °C | 7.1 mm²/s | |
| 600.0 °C | 5.8 mm²/s | |
Listrik
| Sifat | Suhu | Nilai |
|---|
| Resistivitas listrik | 20.0 °C | 1.2E-7 - 2.5E-7 Ω·m |
| 100.0 °C | 2.95E-7 Ω·m |
| 200.0 °C | 3.65E-7 Ω·m |
| 300.0 °C | 4.53E-7 Ω·m |
| 400.0 °C | 5.56E-7 Ω·m |
| 500.0 °C | 6.74E-7 Ω·m |
| 600.0 °C | 8.13E-7 Ω·m |
Sifat Kimia
| Sifat | Nilai |
|---|
| Karbon | 0.47 - 0.55 % |
| Kromium | 0.4 % |
| Mangan | 0.6 - 0.9 % |
| Molibdenum | 0.1 % |
| Nikel | 0.4 % |
| Fosfor | 0.03 - 0.04 % |
| Silikon | 0.4 % |
| Sulfur | 0.035 % |