Baja EN 10273 Grade 13CrMo4-5 – Baja Suhu Tinggi Normalisasi & Penyahperasan

Baja 13CrMo4-5 adalah baja suhu tinggi. Aplikasi: konstruksi boiler untuk superheater dan saluran uap panas, untuk kolektor, flange dan leher las leleh, dan dalam konstruksi aparatur di petrokimia.

Sifat-sifat

Umum

Properti	Suhu	Nilai
Kepadatan	20.0 °C	7.85 g/cm³
	50.0 °C	7.84 g/cm³
	100.0 °C	7.82 g/cm³
	150.0 °C	7.81 g/cm³
	200.0 °C	7.79 g/cm³
	250.0 °C	7.77 g/cm³
	300.0 °C	7.76 g/cm³
	350.0 °C	7.74 g/cm³
	400.0 °C	7.72 g/cm³
	450.0 °C	7.7 g/cm³
	500.0 °C	7.68 g/cm³
	550.0 °C	7.66 g/cm³
	600.0 °C	7.64 g/cm³

Mekanikal

Properti	Suhu	Nilai
Modul elastis	-100.0 °C	217 GPa
	20.0 °C	212 - 212.48 GPa
	50.0 °C	211.6 GPa
	100.0 °C	207 - 208.95 GPa
	150.0 °C	205.52 GPa
	200.0 °C	199 - 201.79 GPa
	250.0 °C	197.67 GPa
	300.0 °C	192 - 193.45 GPa
	350.0 °C	189.23 GPa
	400.0 °C	184 - 184.82 GPa
	450.0 °C	180.41 GPa
	500.0 °C	175 - 175.89 GPa
	550.0 °C	171.28 GPa
	600.0 °C	164 - 166.57 GPa
Peregangan	20.0 °C	19 - 20 %
Rasio Poisson	20.0 °C	0.28 [-]
	50.0 °C	0.28 [-]
	100.0 °C	0.28 [-]
	150.0 °C	0.29 [-]
	200.0 °C	0.29 [-]
	250.0 °C	0.29 [-]
	300.0 °C	0.29 [-]
	350.0 °C	0.3 [-]
	400.0 °C	0.3 [-]
	450.0 °C	0.3 [-]
	500.0 °C	0.3 [-]
	550.0 °C	0.31 [-]
	600.0 °C	0.31 [-]
Modul geser	20.0 °C	82.8 GPa
	50.0 °C	82.4 GPa
	100.0 °C	81.42 GPa
	150.0 °C	79.95 GPa
	200.0 °C	78.38 GPa
	250.0 °C	76.62 GPa
	300.0 °C	74.85 GPa
	350.0 °C	73.08 GPa
	400.0 °C	71.32 GPa
	450.0 °C	69.45 GPa
	500.0 °C	67.59 GPa
	550.0 °C	65.63 GPa
	600.0 °C	63.57 GPa
Kekuatan tarik	20.0 °C	440 - 600 MPa
Kekuatan leleh	20.0 °C	275 - 300 MPa
Kekuatan leleh Rp0.2	50.0 °C	265 - 294 MPa
	100.0 °C	256 - 285 MPa
	150.0 °C	242 - 269 MPa
	200.0 °C	227 - 252 MPa
	250.0 °C	210 - 234 MPa
	300.0 °C	195 - 216 MPa
	350.0 °C	180 - 200 MPa
	400.0 °C	168 - 186 MPa
	450.0 °C	157 - 175 MPa
	500.0 °C	148 - 164 MPa

Termal

Properti	Suhu	Nilai	Komentar
Koefisien ekspansi termal	-100.0 °C	1.05E-5 1/K
	20.0 °C	1.15E-5 1/K
	100.0 °C	1.21E-5 1/K
	200.0 °C	1.27E-5 1/K
	300.0 °C	1.32E-5 1/K
	400.0 °C	1.36E-5 1/K
	500.0 °C	1.4E-5 1/K
	600.0 °C	1.44E-5 1/K
Suhu penggunaan maksimal, jangka panjang		400 - 550 °C
Titik leleh		1382 - 1529 °C	Typikal untuk baja kromium molibdenum
Kalor jenis	-100.0 °C	423 J/(kg·K)
	20.0 °C	461 J/(kg·K)
	100.0 °C	479 J/(kg·K)
	200.0 °C	499 J/(kg·K)
	300.0 °C	517 J/(kg·K)
	400.0 °C	536 J/(kg·K)
	500.0 °C	558 J/(kg·K)
	600.0 °C	587 J/(kg·K)
Konduktivitas termal	20.0 °C	45.9 W/(m·K)
	100.0 °C	46.4 W/(m·K)
	200.0 °C	45.6 W/(m·K)
	300.0 °C	43.5 W/(m·K)
	400.0 °C	40.9 W/(m·K)
	500.0 °C	38.2 W/(m·K)
	600.0 °C	35.5 W/(m·K)
Difusivitas termal	20.0 °C	12.7 mm²/s
	100.0 °C	12 mm²/s
	200.0 °C	11 mm²/s
	300.0 °C	9.9 mm²/s
	400.0 °C	8.7 mm²/s
	500.0 °C	7.3 mm²/s
	600.0 °C	6 mm²/s

Listrik

Properti	Suhu	Nilai
Resistivitas listrik	20.0 °C	2.27E-7 - 2.37E-7 Ω·m
	50.0 °C	2.56E-7 Ω·m
	100.0 °C	2.76E-7 - 2.88E-7 Ω·m
	150.0 °C	3.21E-7 Ω·m
	200.0 °C	3.46E-7 - 3.59E-7 Ω·m
	250.0 °C	4.01E-7 Ω·m
	300.0 °C	4.31E-7 - 4.45E-7 Ω·m
	350.0 °C	4.95E-7 Ω·m
	400.0 °C	5.32E-7 - 5.48E-7 Ω·m
	450.0 °C	6.06E-7 Ω·m
	500.0 °C	6.48E-7 - 6.63E-7 Ω·m
	550.0 °C	7.28E-7 Ω·m
	600.0 °C	7.81E-7 - 7.97E-7 Ω·m

Sifat Kimia

Properti	Nilai
Karbon	0.08 - 0.18 %
Kromium	0.7 - 1.15 %
Tembaga	0.3 %
Mangan	0.4 - 1 %
Molibdenum	0.4 - 0.6 %
Nitrogen	0.01 %
Fosfor	0.03 %
Silikon	0.35 %
Sulfur	0.01 - 0.025 %