Logam
Manufaktur industri
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen)
Umum
| Properti | Suhu | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|---|
| Kepadatan | 20,0 °C | 2,65 g/cm³ | T5 | EN 1706 |
Mekanik
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Modulus elastisitas | 20,0 °C | 74.0 IPK | T5 | EN 1706 | |
| Perpanjangan | -196.0 °C | 0,6% | T5 | EN 1706 | |
| -196.0 °C | 2,4% | T5 | EN 1706 | ||
| -120.0 °C | 0,5% | T5 | EN 1706 | ||
| -120.0 °C | 2,4% | T5 | EN 1706 | ||
| -50,0 °C | 1,0% | T5 | EN 1706 | ||
| -50,0 °C | 2,4% | T5 | EN 1706 | ||
| 20,0 °C | 0,8% | T5 | EN 1706 | ||
| 20,0 °C | 2,2% | T5 | EN 1706 | ||
| 20,0 °C | 2.2 - 2.4 % | T5 | EN 1706 | ||
| 20,0 °C | 2,4% | T5 | EN 1706 | ||
| 220.0 °C | 10,6% | T5 | EN 1706 | ||
| 220.0 °C | 28,4% | T5 | EN 1706 | ||
| 280,0 °C | 30,1% | T5 | EN 1706 | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Cast 3xx.x Series | |||
| Modulus geser | 2.8 IPK | Khas untuk Aluminium Cast 3xx.x Series | |||
| Kekuatan tarik | -196.0 °C | 277.0 MPa | T5 | EN 1706 | |
| -196.0 °C | 304,0 MPa | T5 | EN 1706 | ||
| -120.0 °C | 256,0 MPa | T5 | EN 1706 | ||
| -120.0 °C | 275,0 MPa | T5 | EN 1706 | ||
| -50,0 °C | 246.0 MPa | T5 | EN 1706 | ||
| -50,0 °C | 263,0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 235,0 - 251,0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 235.0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 241,0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 241.0 - 304.0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 251,0 MPa | T5 | EN 1706 | ||
| 20,0 °C | 304,0 MPa | T5 | EN 1706 | ||
| 220.0 °C | 68,0 MPa | T5 | EN 1706 | ||
| 220.0 °C | 75,0 MPa | T5 | EN 1706 | ||
| 280,0 °C | 48,0 MPa | T5 | EN 1706 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 100.0 °C | 2.1e-05 1/K | T5 | EN 1706 | |
| Titik leleh | 505.0 - 770.0 °C | Khas untuk Aluminium Cast 3xx.x Series | |||
| Kapasitas panas spesifik | 20,0 °C | 910.0 J/(kg·K) | T5 | EN 1706 | |
| Konduktivitas termal | 20,0 °C | 150.0 - 170.0 W/(m·K) | T5 | EN 1706 |
Listrik
| Properti | Suhu | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|---|
| Konduktivitas listrik | 20,0 °C | 19000000.0 - 25000000.0 S/m | T5 | EN 1706 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Aluminium | 86,95% | T5 | EN 1706 |
| Tembaga | 0,05 | T5 | EN 1706 |
| Besi | 0,55 | T5 | EN 1706 |
| Memimpin | 0,05 | T5 | EN 1706 |
| Magnesium | 0,2 - 0,45 % | T5 | EN 1706 |
| Mangan | 0,45 | T5 | EN 1706 |
| Nikel | 0,05 | T5 | EN 1706 |
| Silikon | 9,0 - 11,0% | T5 | EN 1706 |
| Timah | 0,05 | T5 | EN 1706 |
| Titanium | 0,15 | T5 | EN 1706 |
| Seng | 0,1 | T5 | EN 1706 |
Properti teknologi
| Properti | ||
|---|---|---|
| Metode pemrosesan | pengecoran cetakan permanen
| |
Logam
Paduan pengecoran aluminium (tekanan die casting) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,65 g/cm³ F EN 1706 Transmisi 20,0 °C 2,65 g/cm³ F EN 1706 Mekanik Properti Suhu Nilai Kondisi Standar Terka
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,65 g/cm³ F EN 1706 Transmisi 20,0 °C 2,65 g/cm³ F EN 1706 Mekanik Propert
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,65 g/cm³ T6 EN 1706 Transmisi 20,0 °C 2,65 g/cm³ T6 EN 1706 Mekanik Prope
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,65 g/cm³ T64 EN 1706 Transmisi 20,0 °C 2,65 g/cm³ T64 EN 1706 Mekanik Pro