Logam
Manufaktur industri
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen, pengecoran mati bertekanan)
Umum
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|---|
| Kepadatan | 2,75 g/cm³ | F | EN 1706 | Transmisi | |
| 20,0 °C | 2,75 g/cm³ | F | EN 1706 |
Mekanik
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk | Komentar |
|---|---|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 60,0 - 90,0 MPa | F | EN 1706 | Transmisi | ||
| Modulus elastisitas | 75.0 IPK | F | EN 1706 | Transmisi | ||
| 20,0 °C | 75.0 IPK | F | EN 1706 | |||
| Kekerasan, Brinell | 60.0 [-] | F | EN 1706 | Transmisi | ||
| 75.0 [-] | F | EN 1706 | Transmisi | |||
| 80.0 [-] | F | EN 1706 | Transmisi | |||
| 20,0 °C | 60.0 [-] | F | EN 1706 | |||
| 20,0 °C | 75.0 [-] | F | EN 1706 | |||
| 20,0 °C | 80.0 [-] | F | EN 1706 | |||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Cast 3xx.x Series | ||||
| Modulus geser | 2.8 IPK | Khas untuk Aluminium Cast 3xx.x Series | ||||
| Kekuatan tarik | 150,0 MPa | F | EN 1706 | Transmisi | ||
| 170.0 MPa | F | EN 1706 | Transmisi | |||
| 240,0 MPa | F | EN 1706 | Transmisi | |||
| 20,0 °C | 150,0 MPa | F | EN 1706 | |||
| 20,0 °C | 170.0 MPa | F | EN 1706 | |||
| 20,0 °C | 240,0 MPa | F | EN 1706 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.1e-05 1/K | F | EN 1706 | Transmisi |
| 100.0 °C | 2.1e-05 1/K | F | EN 1706 | Transmisi | |
| 100 °C | 2.1e-05 1/K | F | EN 1706 | Transmisi | |
| Titik leleh | 490.0 - 600.0 °C | F | EN 1706 | Transmisi | |
| Kapasitas panas spesifik | 880.0 J/(kg·K) | F | EN 1706 | Transmisi | |
| 20,0 °C | 880.0 J/(kg·K) | F | EN 1706 | ||
| Konduktivitas termal | 20,0 °C | 110.0 - 130.0 W/(m·K) | F | EN 1706 | Transmisi |
Listrik
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|---|
| Konduktivitas listrik | 20,0 °C | 14000000.0 - 18000000.0 S/m | F | EN 1706 | Transmisi |
| Resistivitas listrik | 5.56-08 - 7.14-08 ·m | F | EN 1706 | Transmisi |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait | Bentuk |
|---|---|---|---|---|
| Aluminium | 82,55% | F | EN 1706 | |
| Tembaga | 2.0 - 3.5% | F | EN 1706 | Transmisi |
| Besi | 0,8% | F | EN 1706 | |
| 0,80% | F | EN 1706 | Transmisi | |
| Memimpin | 0,25% | F | EN 1706 | Transmisi |
| Magnesium | 0,05 - 0,55 % | F | EN 1706 | Transmisi |
| Mangan | 0,15 - 0,65 % | F | EN 1706 | Transmisi |
| Nikel | 0,35% | F | EN 1706 | Transmisi |
| Silikon | 7,5 - 9,5% | F | EN 1706 | Transmisi |
| Timah | 0,15% | F | EN 1706 | Transmisi |
| Titanium | 0,25% | F | EN 1706 | Transmisi |
| Seng | 1,2 % | F | EN 1706 | Transmisi |
Properti teknologi
| Properti | ||
|---|---|---|
| Anodisasi | dekoratif:tidak disarankan
| |
| Properti korosi | umum:tidak cukup
| |
| Kemampuan mesin umum | setelah perawatan termal:bagus
| |
| Metode pemrosesan | pengecoran cetakan permanen, sampel uji cor secara terpisah
| |
Logam
Paduan pengecoran aluminium (pengecoran pasir, pengecoran cetakan permanen) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan Membungkuk
Paduan pengecoran aluminium (tekanan die casting) Properti Umum Properti Suhu Nilai Kondisi Standar Terkait Bentuk Kepadatan 2,75 g/cm³ F EN 1706 Transmisi 20,0 °C 2,75 g/cm³ F EN 1706 Mekanik Properti Suhu Nilai Kondisi Standar T
Paduan pengecoran aluminium (tekanan die casting) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan Membungkuk 60,0 - 90,0 MPa
Paduan pengecoran aluminium (pengecoran cetakan permanen) Properti Umum Properti Nilai Komentar Kepadatan 2,65 - 2,7 g/cm³ Khas untuk Aluminium Cast 3xx.x Series Mekanik Properti Suhu Nilai Kondisi Standar Terkait Bentuk Komentar Kekuatan Kelelahan Membungkuk 60,0 -