Legam Aluminium Standar AA 6061 T42 dengan Ketahanan Korosi yang Baik

AA 6061 adalah legam yang mudah didapat yang memiliki permukaan yang bagus dan kemampuan untuk dianodisasi. Mudah di-las dan di-brazing dengan permukaan yang rapi. Tahan karat dari air laut dan kondisi atmosfer. Cocok untuk forging panas.

Properti

Umum

Properti	Nilai	Kondisi	Standar terkait
Kepadatan	2.7 g/cm³	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Mekanikal

Properti	Nilai	Kondisi	Standar terkait	Komentar
Modulus elastisitas	69.0 GPa	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Ketahanan retak tingkat (plane-strain)	22.0 - 35.0 MPa·√m			Umum untuk Aluminium Seri 6000 Tawar
Rasio Poisson	0.33 [-]			Umum untuk Aluminium Seri 6000 Tawar
Modulus geser	26.0 - 26.5 GPa			Umum untuk Aluminium Seri 6000 Tawar
Kekuatan tarik	180.0 MPa	T42	Standar AA, ASTM B221, ASTM B241, ASTM B345
	205.0 MPa	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B483

Termal

Properti	Suhu	Nilai	Kondisi	Standar terkait	Komentar
Koefisien ekspansi termal	20 °C	2.36e-05 1/K	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
	100 °C	2.36e-05 1/K	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Titik leleh		580.0 - 650.0 °C	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Kalor jenis		887.0 - 963.0 J/(kg·K)			Umum untuk Aluminium Seri 6000 Tawar
Konduktivitas termal		155.0 - 180.0 W/(m·K)	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Listrik

Properti	Nilai	Kondisi	Standar terkait
Konduktivitas listrik	23000000.0 - 27000000.0 S/m	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Resistivitas listrik	3.7e-08 - 4.35e-08 Ω·m	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Sifat kimia

Properti	Nilai	Kondisi	Standar terkait
Kromium	0.04 - 0.35 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Tembaga	0.15 - 0.4 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Besi	0.70 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Magnesium	0.8 - 1.2 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Mangan	0.15 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Silikon	0.4 - 0.8 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Titanium	0.15 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Seng	0.25 %	T42	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Sifat teknologis

Properti
Pengeloman	umum: mungkin dengan proses dan metode komersial
Sifat korosi	Retak korosi tegangan: tidak ada kerusakan selama operasi dan uji laboratorium (O, T6, T651, T652, T6510, T6511), tidak ada kerusakan selama operasi, kerusakan terbatas selama uji laboratorium (T4, T451, T4510, T4511), umum: baik, tanpa perlindungan di atmosfer industri atau air laut
Kemesinan umum	Umum: buruk (O), cukup (T4, T451, T4510, T4511, T6, T651, T652, T6510, T6511)
Keolahan	umum (kondisi): baik (O), dapat diterima (T4, T451, T4510, T4511), buruk (T6, T651, T652, T6510, T6511)