Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,72 g/cm³ | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 95,0 MPa | O | Standar AA | |
| Modulus elastisitas | 69.0 IPK | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
| Kekerasan, Brinell | 45.0 [-] | O | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 3000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 3000 Tempa | ||
| Modulus geser | 25.0 - 26.0 IPK | Khas untuk Aluminium Seri 3000 Tempa | ||
| Kekuatan tarik | 150.0 - 200.0 MPa | O | Standar AA, ASTM B209, ASTM B313, ASTM B547 | |
| 160.0 - 200,0 MPa | O | Standar AA, ASTM B221 | ||
| 180,0 MPa | O | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.3899999999999998e-05 1/K | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | |
| 100 °C | 2.3899999999999998e-05 1/K | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
| Titik leleh | 630.0 - 655.0 °C | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 | ||
| Kapasitas panas spesifik | 893,0 - 920,0 J/(kg·K) | Khas untuk Aluminium Seri 3000 Tempa | |||
| Konduktivitas termal | 163 W/(m·K) | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 24000000.0 S/m | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Resistivitas listrik | 4.17e-08 ·m | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Tembaga | 0,25% | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Besi | 0,70% | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Magnesium | 0,8 - 1,3 % | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Mangan | 1,0 - 1,5% | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Silikon | 0,3% | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
| Seng | 0,25% | O | Standar AA, ASTM B209, ASTM B221, ASTM B313, ASTM B547 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:Lötbar mit speziellen Techniken oder bei bestimmten Anwendungen
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:kurang (O, H32), cukup (H34, H36, H38)
| |
| Kemampuan Kerja | umum (kondisi):baik (O), dapat diterima (H32, H34), buruk (H36, H38)
| |
Logam
Aluminium Alloy AA 2219, paduan yang tahan lama diproduksi dengan aditif tembaga. Ini terkenal karena kekuatan strukturalnya yang sangat baik dan digunakan untuk berbagai aplikasi suhu tinggi. Ini adalah paduan yang cocok untuk banyak proses pengerjaan logam termasuk pemesinan, pembentukan, perlakua
Aluminium AA 5086 adalah paduan struktural, yang menawarkan ketahanan korosi yang kuat kepada pengguna dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat dengan pengerasan noda dan pengerjaan dingin, sambil tetap menja
AA 7075 adalah paduan kekuatan tinggi yang menawarkan ketahanan retak korosi tegangan yang baik. Dikenal sebagai andalan dalam industri kedirgantaraan sejak diperkenalkan, Aluminium 7075 menghadirkan ketangguhan moderat serta rasio kekuatan-terhadap-berat yang sangat baik. Penting juga untuk dicatat
AA 6061 adalah paduan yang tersedia yang memiliki permukaan akhir yang baik dan kemampuan untuk dianodisasi.Kemudahan las dan brazability dengan permukaan akhir yang bagus. Ketahanan terhadap korosi dari air laut dan kondisi atmosfer. Cocok untuk penempaan panas. Properti Umum Properti Nilai Ko