AA Standar Grade 7075 T6

AA 7075 adalah paduan kekuatan tinggi yang menawarkan ketahanan retak korosi tegangan yang baik. Dikenal sebagai andalan dalam industri kedirgantaraan sejak diperkenalkan, Aluminium 7075 menghadirkan ketangguhan moderat serta rasio kekuatan-terhadap-berat yang sangat baik. Penting juga untuk dicatat bahwa pada suhu di bawah nol, kekuatan Aluminium 7075 meningkat.

Layanan tambahan: Stek, Bagian dari gambar

STEEL SCOUT

DISTRIBUTOR

Informasi dan layanan

Jumlah: 1 PCS

Kepadatan

2,81 g/cm³

Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Mekanik

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Kelelahan Membungkuk	160.0 MPa	T6	Standar AA
Modulus elastisitas	72.0 IPK	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Kekerasan, Brinell	150.0 [-]	T6	Standar AA
Ketangguhan Retak Bidang-Strain	22.0 - 35.0 MPa·√m			Khas untuk Aluminium Seri 7000 Tempa
Rasio Poisson	0.33 [-]			Khas untuk Aluminium Seri 7000 Tempa
Modulus geser	26.4 - 27.1 IPK			Khas untuk Aluminium Seri 7000 Tempa
Kekuatan tarik	450,0 MPa	T6	Standar AA, ASTM B247
	455.0 MPa	T6	Standar AA, ASTM B247
	470.0 MPa	T6	Standar AA, ASTM B247
	475,0 MPa	T6	Standar AA, ASTM B247
	485.0 MPa	T6	Standar AA, ASTM B247
	490.0 MPa	T6	Standar AA, ASTM B247
	495.0 MPa	T6	Standar AA, ASTM B247
	505,0 MPa	T6	Standar AA, ASTM B247
	510.0 MPa	T6	Standar AA, ASTM B209, ASTM B247
	515,0 MPa	T6	Standar AA, ASTM B247
	525.0 MPa	T6	Standar AA, ASTM B209
	530.0 MPa	T6	Standar AA, ASTM B210, ASTM B211, ASTM B316
	540.0 MPa	T6	Standar AA, ASTM B209, ASTM B221, ASTM B241
	560.0 MPa	T6	Standar AA, ASTM B221, ASTM B241
	570.0 MPa	T6	Standar AA

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien ekspansi termal	20 °C	2.36e-05 1/K	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
	100 °C	2.36e-05 1/K	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Titik leleh		475.0 - 635.0 °C	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Kapasitas panas spesifik		795,0 - 1050,0 J/(kg·K)			Khas untuk Aluminium Seri 7000 Tempa
Konduktivitas termal		130 W/(m·K)	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas listrik	19000000.0 S/m	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Resistivitas listrik	5.26e-08 ·m	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Sifat kimia

Properti	Nilai	Kondisi	Standar Terkait
Kromium	0,18 - 0,28%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Tembaga	1.2 - 2.0 %	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Besi	0,50 %	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Magnesium	2,1 - 2,9%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Mangan	0,3%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Silikon	0,4%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Titanium	0,2%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316
Seng	5.1 - 6.1%	T6	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B316

Properti teknologi

Properti
Mematri	umum:tidak ada pematrian yang diketahui atau dikembangkan
Properti korosi	Retak korosi tegangan:Kerusakan operasional di area dengan tegangan tarik melintang terhadap struktur butir, kerusakan terbatas pada sampel laboratorium, umum:baik, tanpa perlindungan di atmosfer industri atau air laut
Kemampuan mesin umum	Umum:buruk (O), baik hingga dapat diterima
Kemampuan Kerja	umum (kondisi):tidak sesuai

EN 573-3 Kelas AW-6063 T66 EN 573-3 Kelas AW-7022 T6510