AA 5086 Aluminum: Legas Struktur Tahan Korosi dan Kekuatan Tinggi

Aluminium AA 5086 adalah legas struktur yang menawarkan ketahanan korosi yang baik dan konduktivitas listrik tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dibanding 5052 atau 5083, AA 5086 menjadi lebih kuat melalui pengeringan secara strain dan pengolahan dingin, sambil tetap menjadi pilihan yang hemat biaya. Legas ini dapat dipasang dengan metode konvensi, meskipun las busa listrik disarankan.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Densitas	2.66 g/cm³	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547

Mekanis

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Modul elastisitas	71.0 GPa	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547	-
Kekuatan retakan stensilasi datar	22.0 - 35.0 MPa·√m	-	-	Typikal untuk aluminium serangkaian 5000 tiraman
Rasio Poisson	0.33 [-]	-	-	Typikal untuk aluminium serangkaian 5000 tiraman
Modul geser	26.0 - 26.5 GPa	-	-	Typikal untuk aluminium serangkaian 5000 tiraman
Kekuatan tarik	240.0 - 305.0 MPa	O	Standar AA, ASTM B209, ASTM B313, ASTM B547	-
Kekuatan tarik	240.0 - 315.0 MPa	O	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345	-
Kekuatan tarik	260.0 MPa	O	Standar AA	-

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien ekspansi termal	20 °C	2.38e-05 1/K	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547	-
Koefisien ekspansi termal	100 °C	2.38e-05 1/K	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547	-
Suhu operasi maksimal	-	150.0 °C	-	-	Typikal untuk aluminium serangkaian 5000 tiraman
Titik leleh	-	585.0 - 640.0 °C	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547	-
Kapasitas panas spesifik	-	879.0 - 963.0 J/(kg·K)	-	-	Typikal untuk aluminium serangkaian 5000 tiraman
Konduktivitas termal	-	126 W/(m·K)	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547	-

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas listrik	18.000.000,0 S/m	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Resistivitas listrik	5,56e-08 Ω·m	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547

Sifat Kimia

Properti	Nilai	Kondisi	Standar Terkait
Kromium	0,05 - 0,25 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Tembaga	0,1 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Besi	0,50 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Magnesium	3,5 - 4,5 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Mangan	0,2 - 0,7 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Silikon	0,4 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Titanium	0,15 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547
Seng	0,25 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B221, ASTM B241, ASTM B313, ASTM B345, ASTM B547

Sifat Teknologis

Properti
Losen	umum: tidak ada losen yang diketahui atau dikembangkan
Sifat korosi	Retakan korosi stres: tidak ada kerusakan selama operasi dan uji laboratorium (O, H32, H116, H111), tidak ada kerusakan selama operasi, kerusakan terbatas selama uji laboratorium (H34, H36, H38), umum: sangat baik, tanpa perlindungan di atmosfer industri atau laut
Kerajinan umum	Umum: buruk (O, H32, H116, H111), cukup (H34, H36, H38)
Kerasibilitas	umum (kondisi): baik (O), dapat diterima (H32, H116, H111), buruk (H36, H38)