Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,705 g/cm³ | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 30.0 MPa | H12 | Standar AA | |
| Modulus elastisitas | 69.0 IPK | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 | |
| Kekerasan, Brinell | 23.0 [-] | H12 | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 1000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 1000 Tempa | ||
| Modulus geser | 25.9 IPK | Khas untuk Aluminium Seri 1000 Tempa | ||
| Kekuatan tarik | 70.0 MPa | H12 | Standar AA, ASTM B210, ASTM B483 | |
| 75,0 - 110,0 MPa | H12 | Standar AA, ASTM B209 | ||
| 85,0 MPa | H12 | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.36e-05 1/K | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 | |
| 100 °C | 2.36e-05 1/K | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 | ||
| Titik leleh | 645.0 - 655.0 °C | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 | ||
| Kapasitas panas spesifik | 900,0 - 963,0 J/(kg·K) | Khas untuk Aluminium Seri 1000 Tempa | |||
| Konduktivitas termal | 230.0 - 234.0 W/(m·K) | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 35000000.0 - 36000000.0 S/m | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Resistivitas listrik | 2.78-08 - 2.86-08 ·m | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Aluminium | 99,6% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Tembaga | 0,05% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Besi | 0,35% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Magnesium | 0,03 % | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Mangan | 0,03 % | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Silikon | 0,25% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Titanium | 0,03 % | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Vanadium | 0,05% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
| Seng | 0,05% | H12 | Standar AA, ASTM B209, ASTM B210, ASTM B483 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:mungkin dengan proses dan metode komersial
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:tidak sesuai (O, H12), buruk (H14, H16, H18)
| |
| Kemampuan Kerja | umum (kondisi):baik (O, H12, H14), dapat diterima (H16, H18)
| |
Logam
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,705 g/cm³ H14 Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B483 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 35,0 MPa H14 Standar AA Modulu
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,69 g/cm³ O Standar AA, ASTM B209, ASTM B210, ASTM B313, ASTM B483, ASTM B547 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 85,0 MPa O Standar AA Modulus ela
Aluminium AA 3003 adalah paduan populer yang menawarkan ketahanan korosi atmosferik yang sangat baik kepada pelanggan dan kekuatan sedang. Aluminium 3003 menawarkan kemampuan mesin yang baik untuk paduan aluminium, meskipun tidak dapat diolah dengan panas. Tidak seperti paduan aluminium lainnya, AA
AA 1100 adalah paduan yang lembut, tidak dapat diolah dengan panas, dan berkekuatan rendah yang menawarkan ketahanan korosi yang kuat. Terdiri dari 99% aluminium dan 0,12% tembaga, AA 1100 adalah paduan aluminium kelas paling murni yang tersedia secara komersial. Properti Umum Properti Nila