Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,705 g/cm³ | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Modulus elastisitas | 69.0 IPK | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 1000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 1000 Tempa | ||
| Modulus geser | 25.9 IPK | Khas untuk Aluminium Seri 1000 Tempa | ||
| Kekuatan tarik | 60,0 MPa | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
| 70.0 MPa | H112 | Standar AA, ASTM B209 | ||
| 75,0 MPa | H112 | Standar AA, ASTM B209 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.36e-05 1/K | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | |
| 100 °C | 2.36e-05 1/K | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | ||
| Titik leleh | 645.0 - 655.0 °C | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 | ||
| Kapasitas panas spesifik | 900,0 - 963,0 J/(kg·K) | Khas untuk Aluminium Seri 1000 Tempa | |||
| Konduktivitas termal | 230.0 - 234.0 W/(m·K) | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 35000000.0 - 36000000.0 S/m | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Resistivitas listrik | 2.78-08 - 2.86-08 ·m | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Aluminium | 99,6% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Tembaga | 0,05% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Besi | 0,35% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Magnesium | 0,03 % | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Mangan | 0,03 % | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Silikon | 0,25% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Titanium | 0,03 % | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Vanadium | 0,05% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
| Seng | 0,05% | H112 | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B345 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:mungkin dengan proses dan metode komersial
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:tidak sesuai (O, H12), buruk (H14, H16, H18)
| |
| Kemampuan Kerja | umum (kondisi):baik (O, H12, H14), dapat diterima (H16, H18)
| |
Logam
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,66 g/cm³ H112 Standar AA, ASTM B209, ASTM B211, ASTM B221 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 115,0 MPa H112 Standar AA Modulus elastisitas 70.
Aluminium AA 3003 adalah paduan populer yang menawarkan ketahanan korosi atmosferik yang sangat baik kepada pelanggan dan kekuatan sedang. Aluminium 3003 menawarkan kemampuan mesin yang baik untuk paduan aluminium, meskipun tidak dapat diolah dengan panas. Tidak seperti paduan aluminium lainnya, AA
AA 1100 adalah paduan yang lembut, tidak dapat diolah dengan panas, dan berkekuatan rendah yang menawarkan ketahanan korosi yang kuat. Terdiri dari 99% aluminium dan 0,12% tembaga, AA 1100 adalah paduan aluminium kelas paling murni yang tersedia secara komersial. Properti Umum Properti Nila
Aluminium AA 5086 adalah paduan struktural, yang menawarkan ketahanan korosi yang kuat kepada pengguna dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat dengan pengerasan noda dan pengerjaan dingin, sambil tetap menja