Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,66 g/cm³ | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 115,0 MPa | H112 | Standar AA | |
| Modulus elastisitas | 70.0 IPK | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 | |
| Kekerasan, Brinell | 63.0 [-] | H112 | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 5000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 5000 Tempa | ||
| Modulus geser | 26.0 - 26.5 IPK | Khas untuk Aluminium Seri 5000 Tempa | ||
| Kekuatan tarik | 205,0 MPa | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 | |
| 210.0 MPa | H112 | Standar AA, ASTM B209 | ||
| 220.0 MPa | H112 | Standar AA, ASTM B209 | ||
| 240,0 MPa | H112 | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.3899999999999998e-05 1/K | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 | |
| 100 °C | 2.3899999999999998e-05 1/K | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 | ||
| Suhu layanan maksimum | 150,0 °C | Khas untuk Aluminium Seri 5000 Tempa | |||
| Titik leleh | 590.0 - 645.0 °C | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 | ||
| Kapasitas panas spesifik | 879.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Seri 5000 Tempa | |||
| Konduktivitas termal | 126 W/(m·K) | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 19000000.0 S/m | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Resistivitas listrik | 5.26e-08 ·m | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kromium | 0,15 - 0,35 % | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Tembaga | 0,1% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Besi | 0,40% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Magnesium | 3,1 - 3,9% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Mangan | 0,1% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Silikon | 0,25% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Titanium | 0,2% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
| Seng | 0,2% | H112 | Standar AA, ASTM B209, ASTM B211, ASTM B221 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:tidak ada pematrian yang diketahui atau dikembangkan
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:kurang (O, H32), cukup (H34, H36, H38)
| |
| Kemampuan Kerja | umum (kondisi):baik (O), dapat diterima (H32, H34), buruk (H36, H38)
| |
Logam
Properti Umum Properti Nilai Kondisi Standar Terkait Kepadatan 2,66 g/cm³ O Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B313, ASTM B547 Mekanik Properti Nilai Kondisi Standar Terkait Komentar Kekuatan Kelelahan Membungkuk 115,0 MPa O Standar AA
Aluminium AA 3003 adalah paduan populer yang menawarkan ketahanan korosi atmosferik yang sangat baik kepada pelanggan dan kekuatan sedang. Aluminium 3003 menawarkan kemampuan mesin yang baik untuk paduan aluminium, meskipun tidak dapat diolah dengan panas. Tidak seperti paduan aluminium lainnya, AA
AA 1100 adalah paduan yang lembut, tidak dapat diolah dengan panas, dan berkekuatan rendah yang menawarkan ketahanan korosi yang kuat. Terdiri dari 99% aluminium dan 0,12% tembaga, AA 1100 adalah paduan aluminium kelas paling murni yang tersedia secara komersial. Properti Umum Properti Nila
Aluminium AA 5086 adalah paduan struktural, yang menawarkan ketahanan korosi yang kuat kepada pengguna dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat dengan pengerasan noda dan pengerjaan dingin, sambil tetap menja