Legam Aluminium AA 3003: Grade 3003 H112 – Ketahanan Korosi Tinggi dan Kemampuan Las yang Baik

Aluminium AA 3003 adalah legam populer yang menawarkan pelanggan ketahanan korosi atmosfer yang sangat baik dan kekuatan sedang. Aluminium 3003 menawarkan kemesinan yang baik untuk legam aluminium, meskipun tidak dapat diperlakukan panas. Berbeda dengan legam aluminium lainnya, AA 3003 dapat di-las dengan metode las konvensional. Legam ini juga menerima pengolahan dingin dan panas dengan baik dan secara umum memiliki properti mekanikal yang lebih baik dibandingkan legam aluminium seri 1000.

Properti

Umum

Properti	Nilai	Kondisi	Standar terkait
Kepadatan	2.73 g/cm³	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547

Mekanikal

Properti	Nilai	Kondisi	Standar terkait	Komentar
Modulus elastisitas	69.0 GPa	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Ketahanan retak tingkat (plane-strain)	22.0 - 35.0 MPa·√m			Umum untuk Aluminium Seri 3000 Tawar
Rasio Poisson	0.33 [-]			Umum untuk Aluminium Seri 3000 Tawar
Modulus geser	25.0 - 26.0 GPa			Umum untuk Aluminium Seri 3000 Tawar
Kekuatan tarik	90.0 MPa	H112	Standar AA, ASTM B221
	95.0 MPa	H112	Standar AA, ASTM B211, ASTM B241, ASTM B247, ASTM B345, ASTM B483
	100.0 MPa	H112	Standar AA, ASTM B209
	105.0 MPa	H112	Standar AA, ASTM B209
	115.0 MPa	H112	Standar AA, ASTM B209, ASTM B547

Termal

Properti	Suhu	Nilai	Kondisi	Standar terkait	Komentar
Koefisien ekspansi termal	20 °C	2.3199999999999998e-05 1/K	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
	100 °C	2.3199999999999998e-05 1/K	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Titik leleh		640.0 - 655.0 °C	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Kalor jenis		893.0 - 920.0 J/(kg·K)			Umum untuk Aluminium Seri 3000 Tawar
Konduktivitas termal		159.0 - 193.0 W/(m·K)	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547

Listrik

Properti	Nilai	Kondisi	Standar terkait
Konduktivitas listrik	24000000.0 - 29000000.0 S/m	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Resistivitas listrik	3.45e-08 - 4.17e-08 Ω·m	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547

Sifat kimia

Properti	Nilai	Kondisi	Standar terkait
Tembaga	0.05 - 0.2 %	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Besi	0.70 %	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Mangan	1.0 - 1.5 %	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Silikon	0.6 %	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547
Seng	0.1 %	H112	Standar AA, ASTM B209, ASTM B211, ASTM B221, ASTM B241, ASTM B247, ASTM B345, ASTM B483, ASTM B547

Sifat teknologis

Properti
Pengeloman	umum: mungkin dengan proses dan metode komersial
Sifat korosi	Retak korosi tegangan: tidak ada kerusakan selama operasi dan uji laboratorium, umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Kemesinan umum	Umum: tidak cocok (O, H12), buruk (H14, H16, H25)
Keolahan	umum (kondisi): baik (O, H12), dapat diterima (H14, H25), buruk (H16, H18)