Aluminium AA 5052 adalah paduan non-panas dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang paling umum dan sebenarnya menawarkan beberapa karakteristik pengelasan terbaik dari semua paduan aluminium.
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,68 g/cm³ | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 110,0 MPa | O | Standar AA | |
| Modulus elastisitas | 70.0 IPK | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| Kekerasan, Brinell | 47.0 [-] | O | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 5000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 5000 Tempa | ||
| Modulus geser | 26.0 - 26.5 IPK | Khas untuk Aluminium Seri 5000 Tempa | ||
| Kekuatan tarik | 170.0 - 215.0 MPa | O | Standar AA, ASTM B209, ASTM B313, ASTM B547 | |
| 170.0 - 240,0 MPa | O | Standar AA, ASTM B210, ASTM B221, ASTM B241 | ||
| 170.0 - 220.0 MPa | O | Standar AA, ASTM B211 | ||
| 170.0 MPa | O | Standar AA, ASTM B483 | ||
| 195,0 MPa | O | Standar AA | ||
| 220.0 MPa | O | Standar AA, ASTM B316 |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.38e-05 1/K | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | |
| 100 °C | 2.38e-05 1/K | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
| Suhu layanan maksimum | 150,0 °C | Khas untuk Aluminium Seri 5000 Tempa | |||
| Titik leleh | 605,0 - 650,0 °C | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 | ||
| Kapasitas panas spesifik | 879.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Seri 5000 Tempa | |||
| Konduktivitas termal | 138 W/(m·K) | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 20000000.0 S/m | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Resistivitas listrik | 5e-08 ·m | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kromium | 0,15 - 0,35 % | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Tembaga | 0,1% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Besi | 0,40% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Magnesium | 2.2 - 2.8% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Mangan | 0,1% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Silikon | 0,25% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
| Seng | 0,1% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:mematri terbatas
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:kurang (O, H32), cukup (H34, H36, H38)
| |
| Kemampuan Kerja | umum (kondisi):baik (O), dapat diterima (H32, H34), buruk (H36, H38)
| |
Logam
Aluminium AA 5052 adalah paduan non-panas yang dapat diolah dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang pal
Aluminium AA 5052 adalah paduan non-panas yang dapat diolah dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang pal
Aluminium AA 5052 adalah paduan non-panas yang dapat diolah dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang pal
Aluminium AA 5052 adalah paduan non-panas yang dapat diolah dengan kualitas finishing yang sangat baik. AA 5052 menawarkan ketahanan korosi yang lebih baik daripada kebanyakan paduan aluminium, terutama untuk air asin dan atmosfer laut. Paduan ini dapat dengan mudah dilas menggunakan teknik yang pal