| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,705 g/cm³ | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 20.0 MPa | O | Standar AA | |
| Modulus elastisitas | 69.0 IPK | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| Kekerasan, Brinell | 19.0 [-] | O | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 1000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 1000 Tempa | ||
| Modulus geser | 25.9 IPK | Khas untuk Aluminium Seri 1000 Tempa | ||
| Kekuatan tarik | 55,0 - 95,0 MPa | O | Standar AA, ASTM B209 | |
| 55,0 MPa | O | Standar AA, ASTM B211 | ||
| 60,0 - 95,0 MPa | O | Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| 70.0 MPa | O | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.36e-05 1/K | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | |
| 100 °C | 2.36e-05 1/K | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| Titik leleh | 645.0 - 655.0 °C | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 | ||
| Kapasitas panas spesifik | 900,0 - 963,0 J/(kg·K) | Khas untuk Aluminium Seri 1000 Tempa | |||
| Konduktivitas termal | 230.0 - 234.0 W/(m·K) | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 35000000.0 - 36000000.0 S/m | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Resistivitas listrik | 2.78-08 - 2.86-08 ·m | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Aluminium | 99,6% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Tembaga | 0,05% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Besi | 0,35% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Magnesium | 0,03 % | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Mangan | 0,03 % | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Silikon | 0,25% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Titanium | 0,03 % | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Vanadium | 0,05% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
| Seng | 0,05% | O | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B221, ASTM B241, ASTM B345, ASTM B483 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:mungkin dengan proses dan metode komersial
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:tidak sesuai (O, H12), buruk (H14, H16, H18)
| |
| Kemampuan Kerja | umum (kondisi):baik (O, H12, H14), dapat diterima (H16, H18)
| |
Logam
Aluminium Alloy AA 2219, paduan yang tahan lama diproduksi dengan aditif tembaga. Ini terkenal karena kekuatan strukturalnya yang sangat baik dan digunakan untuk berbagai aplikasi suhu tinggi. Ini adalah paduan yang cocok untuk banyak proses pengerjaan logam termasuk pemesinan, pembentukan, perlakua
Aluminium AA 5086 adalah paduan struktural, yang menawarkan ketahanan korosi yang kuat kepada pengguna dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat dengan pengerasan noda dan pengerjaan dingin, sambil tetap menja
AA 7075 adalah paduan kekuatan tinggi yang menawarkan ketahanan retak korosi tegangan yang baik. Dikenal sebagai andalan dalam industri kedirgantaraan sejak diperkenalkan, Aluminium 7075 menghadirkan ketangguhan moderat serta rasio kekuatan-terhadap-berat yang sangat baik. Penting juga untuk dicatat
AA 6061 adalah paduan yang tersedia yang memiliki permukaan akhir yang baik dan kemampuan untuk dianodisasi.Kemudahan las dan brazability dengan permukaan akhir yang bagus. Ketahanan terhadap korosi dari air laut dan kondisi atmosfer. Cocok untuk penempaan panas. Properti Umum Properti Nilai Ko