Logam
Manufaktur industri
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,69 g/cm³ | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Modulus elastisitas | 70.0 IPK | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
| Kekerasan, Brinell | 62.0 [-] | O | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Seri 5000 Tempa | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Seri 5000 Tempa | ||
| Modulus geser | 26.0 - 26.5 IPK | Khas untuk Aluminium Seri 5000 Tempa | ||
| Kekuatan tarik | 215.0 - 285.0 MPa | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
| 250,0 MPa | O | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.36e-05 1/K | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | |
| 100 °C | 2.36e-05 1/K | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
| Suhu layanan maksimum | 150,0 °C | Khas untuk Aluminium Seri 5000 Tempa | |||
| Titik leleh | 600,0 - 645,0 °C | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 | ||
| Kapasitas panas spesifik | 879.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Seri 5000 Tempa | |||
| Konduktivitas termal | 134 W/(m·K) | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 20000000.0 S/m | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Resistivitas listrik | 5e-08 ·m | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kromium | 0,05 - 0,2 % | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Tembaga | 0,1% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Besi | 0,40% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Magnesium | 2,4 - 3,0% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Mangan | 0,5 - 1,0% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Silikon | 0,25% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Titanium | 0,2% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
| Seng | 0,25% | O | Standar AA, ASTM B209, ASTM B221, ASTM B241, ASTM B547 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:tidak ada pematrian yang diketahui atau dikembangkan
| |
| Properti korosi | Retak korosi tegangan:tidak ada kerusakan selama operasi dan uji laboratorium, umum:sangat baik, tanpa perlindungan di atmosfer industri atau air laut
| |
| Kemampuan mesin umum | Umum:buruk (O, H32, H111), cukup (H34)
| |
| Kemampuan Kerja | umum (kondisi):baik (O), dapat diterima (H32, H34, H111)
| |
Logam
Aluminium AA 6063 adalah paduan arsitektur yang menawarkan ketahanan tinggi terhadap korosi dan karakteristik finishing yang sangat baik kepada pengguna. Mudah diekstrusi dengan kemampuan mesin yang baik, AA 6063 dapat dibentuk panas dan dingin dan umumnya tersedia sebagai temper T6 serta temper T4.
AA 6061 adalah paduan yang tersedia yang memiliki permukaan akhir yang baik dan kemampuan untuk dianodisasi.Kemudahan las dan brazability dengan permukaan akhir yang bagus. Ketahanan terhadap korosi dari air laut dan kondisi atmosfer. Cocok untuk penempaan panas. Properti Umum Properti Nilai Ko
Aluminium AA 2024, yang dikenal penggunaannya dalam industri pesawat terbang, merupakan paduan yang menawarkan kekuatan yang sangat baik. Ketika dalam kondisi anil itu mudah dibentuk dan memiliki kemampuan mesin yang baik. Meskipun memiliki tingkat ketahanan korosi yang relatif rendah, ia dapat dike
Aluminium AA 5005 adalah paduan magnesium aluminium ramping dengan kepadatan rendah dan konduktivitas termal yang sangat baik. Paduan non-panas yang tidak dapat diolah dengan kekuatan sedang ini dikenal karena ketahanannya terhadap korosi dalam situasi laut alkali. Aluminium AA 5005 mudah dikerjakan