SAE J2329 Grade 4 Baja Dilapis Dingin – Properti & Performa

Properti

Umum

Properti	Suhu	Nilai	Komentar
Kepadatan	23.0 °C	7.8 - 7.9 g/cm³	Typical for Low Carbon Steel

Mekanis

Properti	Suhu	Nilai	Komentar
Modulus elastis	23.0 °C	200 - 215 GPa	Typical for Low Carbon Steel
Regangan	23.0 °C	40 %
Rasio Poisson	23.0 °C	0.29 [-]	Typical for Low Carbon Steel
Modulus geser	23.0 °C	82 GPa	Typical for Low Carbon Steel
Kekuatan tarik	23.0 °C	270 MPa
Kekuatan leleh	23.0 °C	140 - 185 MPa

Termal

Properti	Suhu	Nilai	Komentar
Koefisien ekspansi termal	23.0 °C	1.32E-5 - 1.38E-5 1/K	Typical for Low Carbon Steel
Suhu operasi maksimum		500 °C	Typical for Carbon Steel
Titik leleh		1480 - 1526 °C	Typical for Low Carbon Steel
Kapasitas panas spesifik	23.0 °C	465 J/(kg·K)	Typical for Low Carbon Steel
Konduktivitas termal	23.0 °C	25 - 93 W/(m·K)	Typical for Low Carbon Steel

Listrik

Properti	Suhu	Nilai	Komentar
Resistivitas listrik	23.0 °C	1.43E-7 - 1.74E-7 Ω·m	Typical for Carbon Steel

Magnetik

Properti	Nilai	Komentar
Suhu Curie	770 °C	Typical for Low Carbon Steel

Properti Kimia

Properti	Nilai
Aluminium	0.02 %
Karbon	0.08 %
Besi	balance
Mangan	0.4 %
Fosfor	0.03 %
Sulfur	0.025 %
Yttrium	0.02 %