SEW 400 – Baja X2CrNiMo13‑4, Quenched & Tempered (QT) – Grade Tahan Korat Tinggi Performa

Tentang Bahan

Baja X2CrNiMo13-4 (1.4320) digunakan untuk layanan gas sour sesuai dengan NACE MR0175.

Properti	Suhu	Nilai
Kepadatan	20.0 °C	7.7 g/cm³

Properti	Suhu	Nilai	Keterangan
Modul elastisitas	20.0 °C	198 GPa
	100.0 °C	193 GPa
	200.0 °C	183 GPa
	300.0 °C	175 GPa
	400.0 °C	172 GPa
	500.0 °C	159 GPa
Regangan	20.0 °C	17 %
Regangan, melintang	20.0 °C	15 %
Kekejaman, Brinell	20.0 °C	255 [-]
Kekejaman, Brinell, melintang	20.0 °C	255 [-]
Rasio Poisson	23.0 °C	0.3 [-]	Typical for Austenitic Stainless Steel
Modul geser	23.0 °C	77 GPa	Typical for Austenitic Stainless Steel
Kekuatan tarik	20.0 °C	680 - 880 MPa
Kekuatan tarik, melintang	20.0 °C	680 - 880 MPa
Tegangan leleh Rp0.2	20.0 °C	520 MPa
	50.0 °C	500 MPa
	100.0 °C	490 MPa
	150.0 °C	480 MPa
	200.0 °C	470 MPa
	250.0 °C	460 MPa
	300.0 °C	450 MPa
Tegangan leleh Rp0.2, melintang	20.0 °C	520 MPa

Properti	Suhu	Nilai	Keterangan
Koefisien ekspansi termal	100.0 °C	1.17E-5 1/K
	200.0 °C	1.23E-5 1/K
	300.0 °C	1.26E-5 1/K
Titik leleh		1230 - 1480 °C	Typical for Austenitic Stainless Steel
Kalor jenis	20.0 °C	430 J/(kg·K)
Konduktivitas termal	20.0 °C	25 W/(m·K)

Properti	Suhu	Nilai	Keterangan
Resistivitas listrik	23.0 °C	8.5E-7 Ω·m	Typical for Austenitic Stainless Steel

Logam