Legumi Aluminium AA 6063 T6 – Ketahanan Korosi & Finishing Premium

Aluminium AA 6063 adalah legumi arsitektur yang menawarkan ketahanan korosi yang tinggi dan karakteristik finishing yang luar biasa. Mudah diekstrusi dengan kemampuan pengolahan yang memadai, AA 6063 dapat dibentuk panas maupun dingin dan umumnya tersedia dalam temper T6 serta T4.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Kepadatan	2,7 g/cm³	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Mekanis

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Regangan Lentur	70,0 MPa	T6	Standar AA	-
Modul elastisitas	69,0 GPa	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483	-
Kekerasan, Brinell	73,0 [-]	T6	Standar AA	-
Ketawahan Plane-Strain	22,0 - 35,0 MPa·√m	-	-	Typis untuk Aluminium Seres 6000 Tiarap
Rasio Poisson	0,33 [-]	-	-	Typis untuk Aluminium Seres 6000 Tiarap
Modul geser	26,0 - 26,5 GPa	-	-	Typis untuk Aluminium Seres 6000 Tiarap
Kekuatan regangan	205,0 MPa	T6	Standar AA, ASTM B221, ASTM B241, ASTM B345	-
	230,0 MPa	T6	Standar AA, ASTM B210, ASTM B483	-
	240,0 MPa	T6	Standar AA	-

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien ekspansi termal	20 °C	2,34e-05 1/K	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483	-
	100 °C	2,34e-05 1/K	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483	-
Titik leleh	-	615,0 - 655,0 °C	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483	-
Kapasitas panas spesifik	-	887,0 - 963,0 J/(kg·K)	-	-	Typis untuk Aluminium Seres 6000 Tiarap
Konduktivitas termal	-	193,0 - 218,0 W/(m·K)	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483	-

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas listrik	29.000.000,0 - 34.000.000,0 S/m	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Resistivitas listrik	2,94e-08 - 3,45e-08 Ω·m	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Properti Kimia

Properti	Nilai	Kondisi	Standar Terkait
Kromium	0,1 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Tembaga	0,1 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Besi	0,35 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Magnesium	0,45 - 0,9 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Mangan	0,1 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Silikon	0,2 - 0,6 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Titanium	0,1 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483
Seng	0,1 %	T6	Standar AA, ASTM B210, ASTM B221, ASTM B241, ASTM B345, ASTM B483

Properti Teknologis

Properti
Pengelengan	umum: mungkin dengan proses dan metode komersial
Properti korosi	Retak korosi stres: tidak ada kerusakan selama operasi dan uji laboratorium, umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Kemampuan pengolahan umum	Umum: buruk (T1, T4), cukup (T5, T452, T6, T83, T831, T832)
Kerjabilitas	umum (kondisi): dapat diterima (T1, T4, T5, T452), buruk (T6, T83, T831, T832)

AA 6063 T5: Aluminium Arsitektur Premium dengan Ketahanan Korosi Legasi Standar AA 6061 T651 – Tahan Lama, Tahan Korosi & Mudah Dibentuk