Legasi Aluminium AA 3003 H18 – Ketahanan Korosi Luar Biasa & Keberlasan

Aluminium AA 3003 adalah legasi populer yang menawarkan daya tahan korosi atmosfer yang sangat baik dan kekuatan sedang. Aluminium 3003 menawarkan keberpemesinan yang baik untuk legasi aluminium, meskipun tidak dapat diterawi dengan panas. Berbeda dengan legasi aluminium lainnya, AA 3003 dapat digelas dengan metode pengelasan konvensional. Legasi ini juga dapat diolah secara dingin dan panas dengan baik dan umumnya memiliki properti mekanik yang lebih baik dibandingkan legasi aluminium seri 1000.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Densitas	2.73 g/cm³	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483

Mekanik

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Fatigue Bengkok	70.0 MPa	H18	Standar AA
Modulus Elastisitas	69.0 GPa	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Kekerasan Brinell	55.0	H18	Standar AA
Ketahanan Fraktur Plane-Strain	22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Rasio Poisson	0.33			Typical for Wrought 3000 Series Aluminium
Modul Geser	25.0 - 26.0 GPa			Typical for Wrought 3000 Series Aluminium
Kekuatan Tarik	185.0 MPa	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Kekuatan Tarik	200.0 MPa	H18	Standar AA

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien Ekspansi Termal	20 °C	2.32 × 10⁻⁵ 1/K	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Koefisien Ekspansi Termal	100 °C	2.32 × 10⁻⁵ 1/K	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Titik Leleh		640.0 - 655.0 °C	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Kalor Jenis		893.0 - 920.0 J/(kg·K)			Typical for Wrought 3000 Series Aluminium
Konduktivitas Termal		159.0 - 193.0 W/(m·K)	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas Listrik	24.000.000 - 29.000.000 S/m	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Resistivitas Listrik	3.45e-08 - 4.17e-08 Ω·m	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483

Kimia

Properti	Nilai	Kondisi	Standar Terkait
Tembaga	0.05 - 0.2 %	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Besi	0.70 %	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Mangan	1.0 - 1.5 %	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Silikon	0.6 %	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483
Seng	0.1 %	H18	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B345, ASTM B483

Teknologis

Properti	Keterangan
Pengelelogan (Brazing)	Secara umum: dapat dilakukan dengan proses dan metode komersial
Sifat Korosi	Retak korosi karena tekanan: tidak ada kerusakan selama operasi dan uji laboratorium, secara umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Keberpemesinan Umum	Secara umum: tidak cocok (O, H12), buruk (H14, H16, H25)
Kemudahan Pengolahan	Secara umum (kondisi): baik (O, H12), dapat diterima (H14, H25), buruk (H16, H18)

Legasi Aluminium AA 3003 – Grade H12 Premium untuk Ketahanan Korosi Superior Legasi Aluminium AA 3003 – Ketahanan Korosi Tinggi, Keberpemesinan Baik & Keberlasan

Logam