Legasi Aluminium AA 3003 H14 – Ketahanan Korosi Tinggi & Keberpemesinan Superior

Aluminium AA 3003 adalah legasi populer yang menawarkan daya tahan korosi atmosfer yang sangat baik dan kekuatan sedang. Aluminium 3003 menawarkan keberpemesinan yang baik untuk legasi aluminium, meskipun tidak dapat diterawi dengan panas. Berbeda dengan legasi aluminium lainnya, AA 3003 dapat digelas dengan metode pengelasan konvensional. Legasi ini juga dapat diolah secara dingin dan panas dengan baik dan umumnya memiliki properti mekanik yang lebih baik dibandingkan legasi aluminium seri 1000.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Densitas	2.73 g/cm³	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Mekanik

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Fatigue Bengkok	60.0 MPa	H14	Standar AA
Modulus Elastisitas	69.0 GPa	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kekerasan Brinell	40.0	H14	Standar AA
Ketahanan Fraktur Plane-Strain	22.0 - 35.0 MPa·√m			Typical for Wrought 3000 Series Aluminium
Rasio Poisson	0.33			Typical for Wrought 3000 Series Aluminium
Modul Geser	25.0 - 26.0 GPa			Typical for Wrought 3000 Series Aluminium
Kekuatan Tarik	140.0 - 180.0 MPa	H14	Standar AA, ASTM B209, ASTM B313, ASTM B316, ASTM B547
Kekuatan Tarik	140.0 MPa	H14	Standar AA, ASTM B210, ASTM B211, ASTM B234, ASTM B483
Kekuatan Tarik	150.0 MPa	H14	Standar AA

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien Ekspansi Termal	20 °C	2.32 × 10⁻⁵ 1/K	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Koefisien Ekspansi Termal	100 °C	2.32 × 10⁻⁵ 1/K	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Titik Leleh		640.0 - 655.0 °C	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kalor Jenis		893.0 - 920.0 J/(kg·K)			Typical for Wrought 3000 Series Aluminium
Konduktivitas Termal		159.0 - 193.0 W/(m·K)	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas Listrik	24.000.000 - 29.000.000 S/m	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Resistivitas Listrik	3.45e-08 - 4.17e-08 Ω·m	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Kimia

Properti	Nilai	Kondisi	Standar Terkait
Tembaga	0.05 - 0.2 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Besi	0.70 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Mangan	1.0 - 1.5 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Silikon	0.6 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Seng	0.1 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B234, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Teknologis

Properti	Keterangan
Pengelelogan (Brazing)	Secara umum: dapat dilakukan dengan proses dan metode komersial
Sifat Korosi	Retak korosi karena tekanan: tidak ada kerusakan selama operasi dan uji laboratorium, secara umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Keberpemesinan Umum	Secara umum: tidak cocok (O, H12), buruk (H14, H16, H25)
Kemudahan Pengolahan	Secara umum (kondisi): baik (O, H12), dapat diterima (H14, H25), buruk (H16, H18)

Legasi Aluminium AA 3003 – Ketahanan Korosi Tinggi, Keberpemesinan Baik & Keberlasan Legasi Aluminium AA 3003 H16 – Tahan Korosi, Mudah Diproses & Dapat Digelas