Legung Aluminium AA 1100 H14 – 99% Murni, Tidak Dapat Dirawan Panas dengan Resistensi Korosi Superior

AA 1100 adalah legung lunak, tidak dapat dirawan panas, dan kekuatan rendah yang menawarkan resistensi korosi yang kuat. Dengan komposisi 99% aluminium dan 0,12% tembaga, AA 1100 adalah grade aluminium terurnai yang tersedia secara komersial.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Kepadatan	2,71 g/cm³	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Mekanis

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Lendutan Fatigue	50,0 MPa	H14	Standar AA
Modulus Elastis	69,0 GPa	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kekejaran, Brinell	32,0 [-]	H14	Standar AA
Keawetan Fraktur Tegas	22,0 - 35,0 MPa·√m			Tipikal untuk Aluminium 1000 Series Tiram
Rasio Poisson	0,33 [-]			Tipikal untuk Aluminium 1000 Series Tiram
Modul Geser	25,9 GPa			Tipikal untuk Aluminium 1000 Series Tiram
Kekuatan Tarik	110,0 - 145,0 MPa	H14	Standar AA, ASTM B209, ASTM B313, ASTM B316, ASTM B547
	110,0 MPa	H14	Standar AA, ASTM B210, ASTM B211, ASTM B483
	125,0 MPa	H14	Standar AA

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien Perpanjangan Termal	20 °C	2,36e-05 1/K	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
	100 °C	2,36e-05 1/K	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Titik Leleh		640,0 - 655,0 °C	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kalor Jenis		900,0 - 963,0 J/(kg·K)			Tipikal untuk Aluminium 1000 Series Tiram
Konduktivitas Termal		218,0 - 222,0 W/(m·K)	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas Listrik	33.000.000,0 - 34.000.000,0 S/m	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Resistivitas Listrik	2,94e-08 - 3,03e-08 Ω·m	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Properti Kimia

Properti	Nilai	Kondisi	Standar Terkait
Aluminium	99,0 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Tembaga	0,05 - 0,2 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Mangan	0,05 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Seng	0,1 %	H14	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Properti Teknologis

Properti
Bras	Umum: mungkin dengan proses dan metode komersial
Properti Korosi	Retakan korosi tegangan: tidak ada kerusakan selama operasi dan uji laboratorium, umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Pemesinan Umum	Umum: tidak sesuai (O, H12), buruk (H14, H16, H18)
Keolahan	Umum (kondisi): baik (O, H12, H14), dapat diterima (H16), buruk (H18)