Legung Aluminium AA 1100O – Grade Terurnai dengan Resistensi Korosi Superior

AA 1100 adalah legung lunak, tidak dapat dirawan panas, dan kekuatan rendah yang menawarkan resistensi korosi yang kuat. Dengan komposisi 99% aluminium dan 0,12% tembaga, AA 1100 adalah grade aluminium terurnai yang tersedia secara komersial.

Properti

Umum

Properti	Nilai	Kondisi	Standar Terkait
Kepadatan	2,71 g/cm³	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Mekanis

Properti	Nilai	Kondisi	Standar Terkait	Komentar
Kekuatan Lendutan Fatigue	35,0 MPa	O	Standar AA
Modulus Elastis	69,0 GPa	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kekejaran, Brinell	23,0 [-]	O	Standar AA
Keawetan Fraktur Tegas	22,0 - 35,0 MPa·√m			Tipikal untuk Aluminium 1000 Series Tiram
Rasio Poisson	0,33 [-]			Tipikal untuk Aluminium 1000 Series Tiram
Modul Geser	25,9 GPa			Tipikal untuk Aluminium 1000 Series Tiram
Kekuatan Tarik	75,0 - 105,0 MPa	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B547
	75,0 MPa	O	Standar AA, ASTM B483
	90,0 MPa	O	Standar AA
	110,0 MPa	O	Standar AA, ASTM B316

Termal

Properti	Suhu	Nilai	Kondisi	Standar Terkait	Komentar
Koefisien Perpanjangan Termal	20 °C	2,36e-05 1/K	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
	100 °C	2,36e-05 1/K	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Titik Leleh		640,0 - 655,0 °C	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Kalor Jenis		900,0 - 963,0 J/(kg·K)			Tipikal untuk Aluminium 1000 Series Tiram
Konduktivitas Termal		218,0 - 222,0 W/(m·K)	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Listrik

Properti	Nilai	Kondisi	Standar Terkait
Konduktivitas Listrik	33.000.000,0 - 34.000.000,0 S/m	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Resistivitas Listrik	2,94e-08 - 3,03e-08 Ω·m	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Properti Kimia

Properti	Nilai	Kondisi	Standar Terkait
Aluminium	99,0 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Tembaga	0,05 - 0,2 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Mangan	0,05 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547
Seng	0,1 %	O	Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B313, ASTM B316, ASTM B483, ASTM B547

Properti Teknologis

Properti
Bras	Umum: mungkin dengan proses dan metode komersial
Properti Korosi	Retakan korosi tegangan: tidak ada kerusakan selama operasi dan uji laboratorium, umum: sangat baik, tanpa perlindungan di atmosfer industri atau air laut
Pemesinan Umum	Umum: tidak sesuai (O, H12), buruk (H14, H16, H18)
Keolahan	Umum (kondisi): baik (O, H12, H14), dapat diterima (H16), buruk (H18)

Legung Aluminium AA 1100 H18 – Grade Premium 1100 dengan Resistensi Korosi Superior Legung Aluminium AA 2011 T8 – Standar & Properti

Logam