AA 2014 adalah paduan dengan kekuatan, kemampuan mesin dan kemampuan pengelasan, Aluminium Alloy AA 2014 adalah pilihan yang sangat baik. Ini adalah paduan pengerasan presipitasi yang mempertahankan kekuatan setelah perlakuan panas.
Umum
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kepadatan | 2,8 g/cm³ | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Mekanik
| Properti | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|
| Kekuatan Kelelahan Membungkuk | 125,0 MPa | T6 | Standar AA | |
| Modulus elastisitas | 73.0 IPK | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| Kekerasan, Brinell | 135.0 [-] | T6 | Standar AA | |
| Ketangguhan Retak Bidang-Strain | 22.0 - 35.0 MPa·√m | Khas untuk Aluminium Tempa Seri 2000 | ||
| Rasio Poisson | 0.33 [-] | Khas untuk Aluminium Tempa Seri 2000 | ||
| Modulus geser | 26.0 - 27.5 IPK | Khas untuk Aluminium Tempa Seri 2000 | ||
| Kekuatan tarik | 395.0 MPa | T6 | Standar AA, ASTM B247 | |
| 400,0 MPa | T6 | Standar AA, ASTM B247 | ||
| 405.0 MPa | T6 | Standar AA, ASTM B209, ASTM B247 | ||
| 415,0 MPa | T6 | Standar AA, ASTM B241, ASTM B247 | ||
| 420,0 MPa | T6 | Standar AA, ASTM B247 | ||
| 425.0 MPa | T6 | Standar AA, ASTM B247 | ||
| 435.0 MPa | T6 | Standar AA, ASTM B209, ASTM B247 | ||
| 440.0 MPa | T6 | Standar AA, ASTM B209, ASTM B241, ASTM B247 | ||
| 450,0 MPa | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B247 | ||
| 455.0 MPa | T6 | Standar AA, ASTM B209 | ||
| 460.0 MPa | T6 | Standar AA, ASTM B209 | ||
| 470.0 MPa | T6 | Standar AA, ASTM B241 | ||
| 485.0 MPa | T6 | Standar AA |
Termal
| Properti | Suhu | Nilai | Kondisi | Standar Terkait | Komentar |
|---|---|---|---|---|---|
| Koefisien ekspansi termal | 20 °C | 2.3e-05 1/K | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | |
| 100 °C | 2.3e-05 1/K | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | ||
| Titik leleh | 505.0 - 635.0 °C | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 | ||
| Kapasitas panas spesifik | 816.0 - 963.0 J/(kg·K) | Khas untuk Aluminium Tempa Seri 2000 | |||
| Konduktivitas termal | 134,0 - 193,0 W/(m·K) | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Listrik
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Konduktivitas listrik | 20000000.0 - 29000000.0 S/m | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Resistivitas listrik | 3.45-08 - 5-08 ·m | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Sifat kimia
| Properti | Nilai | Kondisi | Standar Terkait |
|---|---|---|---|
| Kromium | 0,1% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Tembaga | 3,9 - 5,0% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Besi | 0,70% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Magnesium | 0,2 - 0,8% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Mangan | 0,4 - 1,2 % | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Silikon | 0,5 - 1,2 % | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Titanium | 0,15% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
| Seng | 0,25% | T6 | Standar AA, ASTM B209, ASTM B210, ASTM B211, ASTM B241, ASTM B247 |
Properti teknologi
| Properti | ||
|---|---|---|
| Mematri | umum:tidak ada pematrian yang diketahui atau dikembangkan
| |
| Properti korosi | Retak korosi tegangan:Kerusakan operasional di area dengan tegangan tarik melintang terhadap struktur butir, kerusakan terbatas pada sampel laboratorium, umum:cukup, pada prinsipnya harus dilindungi
| |
| Kemampuan mesin umum | Umum:buruk (O), baik hingga dapat diterima
| |
| Kemampuan Kerja | umum (kondisi):buruk(T3, T4, T451), tidak sesuai (T6, T651, T6510, T6511)
| |
Logam
AA 7075 adalah paduan kekuatan tinggi yang menawarkan ketahanan retak korosi tegangan yang baik. Dikenal sebagai andalan dalam industri kedirgantaraan sejak diperkenalkan, Aluminium 7075 menghadirkan ketangguhan moderat serta rasio kekuatan-terhadap-berat yang sangat baik. Penting juga untuk dicatat
AA 6061 adalah paduan yang tersedia yang memiliki permukaan akhir yang baik dan kemampuan untuk dianodisasi.Kemudahan las dan brazability dengan permukaan akhir yang bagus. Ketahanan terhadap korosi dari air laut dan kondisi atmosfer. Cocok untuk penempaan panas. Properti Umum Properti Nilai Ko
AA 2014 adalah paduan dengan kekuatan, kemampuan mesin dan kemampuan pengelasan, Aluminium Alloy AA 2014 adalah pilihan yang sangat baik. Ini adalah paduan pengerasan presipitasi yang mempertahankan kekuatan setelah perlakuan panas. Properti Umum Properti Nilai Kondisi Standar Terkait Ke
AA 2014 adalah paduan dengan kekuatan, kemampuan mesin dan kemampuan pengelasan, Aluminium Alloy AA 2014 adalah pilihan yang sangat baik. Ini adalah paduan pengerasan presipitasi yang mempertahankan kekuatan setelah perlakuan panas. Properti Umum Properti Nilai Kondisi Standar Terkait Ke