AA 5086 H34 Aluminium: Kekuatan & Tahan Korosi Superior untuk Aplikasi Struktural

Aluminium AA 5086 adalah legam struktural yang menawarkan daya tahan korosi yang kuat dan konduktivitas listrik yang tinggi. Menawarkan tingkat kekuatan yang lebih tinggi dari 5052 atau 5083, AA 5086 menjadi lebih kuat melalui pemerasan stain dan kerja dingin, sambil tetap menjadi pilihan yang hemat biaya. Legam ini dapat di-las dengan metode konvensional, meskipun las busa arc dipilih.

Sifat Umum

Sifat	Nilai	Kondisi	Standar Terkait
Masa Jenis	2,66 g/cm³	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Mekanis

Sifat	Nilai	Kondisi	Standar Terkait	Keterangan
Modulus Elastis	71,0 GPa	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Kekuatan Robleh Fraktur Plane-Strain	22,0 - 35,0 MPa·√m			Typical for Wrought 5000 Series Aluminium
Rasio Poisson	0,33 [-]			Typical for Wrought 5000 Series Aluminium
Modulus Geser	26,0 - 26,5 GPa			Typical for Wrought 5000 Series Aluminium
Kekuatan Tarik	300,0 - 350,0 MPa	H34	AA Standards, ASTM B209, ASTM B313, ASTM B547
Kekuatan Tarik	300,0 MPa	H34	AA Standards, ASTM B210
Kekuatan Tarik	325,0 MPa	H34	AA Standards

Sifat Termal

Sifat	Suhu	Nilai	Kondisi	Standar Terkait	Keterangan
Koefisien Perpanjangan Termal	20 °C	2,38e-05 1/K	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Koefisien Perpanjangan Termal	100 °C	2,38e-05 1/K	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Suhu Operasi Maksimum		150,0 °C			Typical for Wrought 5000 Series Aluminium
Titik Leleh		585,0 - 640,0 °C	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Kapasitas Panja Spesifik		879,0 - 963,0 J/(kg·K)			Typical for Wrought 5000 Series Aluminium
Konduktivitas Termal		126 W/(m·K)	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Listrik

Sifat	Nilai	Kondisi	Standar Terkait
Konduktivitas Listrik	18000000,0 S/m	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Resistivitas Listrik	5,56e-08 Ω·m	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Kimia

Unsur	Nilai	Kondisi	Standar Terkait
Kromium	0,05 - 0,25 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Tembaga	0,1 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Besi	0,50 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Magnesium	3,5 - 4,5 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Mangan	0,2 - 0,7 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Silikon	0,4 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Titanium	0,15 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547
Seng	0,25 %	H34	AA Standards, ASTM B209, ASTM B210, ASTM B313, ASTM B547

Sifat Teknologis

Sifat
Brazing	general: no brazing is known or developed
Sifat Korosi	Stress corrosion cracking: no damage during operation and laboratory tests (O, H32, H116, H111), no damage during operation, limited damage during laboratory tests (H34, H36, H38), general: very good, without protection in industrial or seawater atmosphere
General machinability	General: poor (O, H32, H116, H111), sufficient (H34, H36, H38)
Workability	general (condition): good (O), acceptable (H32, H116, H111), poor(H36, H38)